Cementitious compositions and methods of making cementitious compositions
Cementitious compositions having high compressive strength and high flexibility. An efficient method of making such strong cementitious compositions entails pre-mixing cement additives that can easily be added to a mixture of cement, silica, fibers and water. The cementitious compositions can be used to make strong, thin layers, such as tiles, that are relatively lightweight, as well as heavy structures, such as roads and bridges, without additional reinforcement.
1. A cementitious composition, comprising:
a quantity of cement;
a quantity of silica;
a plurality of fibers;
a quantity of water
between 3 ounces and 10 ounces superplasticizer per 100 pounds of the cement and the silica; and
between 3 ounces and 1 quart bonding agent per 100 pounds of the cement and the silica.
2. The cementitious composition of claim 1 , comprising the cement and the silica into a ratio of 1:1.
3. The cementitious composition of claim 1 , comprising up to about 2 gallons of the water per 100 pounds of the cement and the silica.
4. The cementitious composition of claim 1 , wherein the plurality of fibers comprises at least one type of fiber selected from a group consisting of chopped fiberglass E, structural fiberglass, microfiber polypropylene, microfiber polypropylene/polyethylene, and polypropylene microfilaments.
5. The cementitious composition of claim 1 , wherein the plurality of fibers comprises up to about 2 pounds of chopped ½-inch fiberglass per 100 pounds of the cement and the silica and up to about 4 ounces of 2-inch structural fiberglass per 100 pounds of the cement and the silica.
6. The cementitious composition of claim 1 , wherein the plurality of fibers comprises up to about 16 ounces of chopped ½-inch fiberglass per 100 pounds of the cement and the silica, up to about 4 ounces of 2-inch structural fiberglass per 100 pounds of the cement and the silica, and up to 4 ounces of synthetic microfibers per 100 pounds of the cement and the silica.
7. The cementitious composition of claim 1 , further comprising a foam core encapsulated within the composition.
8. The cementitious composition of claim 1 , further comprising between 0.5 quart and 3 quarts set accelerator per 100 pounds of the cement and the silica.
9. The cementitious composition of claim 1 , further comprising between 1.5 ounces and 0.5 quart shrinkage retarder per 100 pounds of the cement and the silica.
10. The cementitious composition of claim 1 , further comprising at least one additive selected from a group consisting of a set accelerator, an air entraining agent, a finishing enhancer, a water reducer, fumed microsilica, metakaolin, and a shrinkage reducer.
11. The cementitious composition of claim 1 , further comprising a dye.
12. A sheet of material, having a thickness of between 0.25 and 0.5 inch, comprising the cementitious composition of claim 1 .
13. A cementitious composition, comprising:
a quantity of cement;
a quantity of silica;
a plurality of fibers;
a quantity of water,
between 3 ounces and 1 quart bonding agent per 100 pounds of the cement and the silica;
between 3 ounces and 2 quarts carboxylated polyether concrete additive per 100 pounds of the cement and the silica; and
between 3 ounces and 1 quart shrinkage retarder per 100 pounds of the cement and the silica.
14. The cementitious composition of claim 13 , comprising the cement and the silica in a ratio of 1:1.
15. The cementitious composition of claim 13 , comprising up to 2 gallons of the water per 100 pounds of the cement and the silica.
16. The cementitious composition of claim 13 , wherein the plurality of fibers comprises at least one type of fiber selected from a group consisting of chopped fiberglass E, structural fiberglass, microfiber polypropylene, microfiber polypropylene/polyethylene, and polypropylene microfilaments.
17. The cementitious composition of claim 13 , wherein the plurality of fibers comprises up to about 16 ounces of chopped ½-inch fiberglass per 100 pounds of the cement and the silica, up to about 4 ounces of 2-inch structural fiberglass per 100 pounds of the cement and the silica, and up to about 4 ounces of synthetic microfibers.
18. The cementitious composition of claim 13 , further comprising between 0.5 quart and 3 quarts set accelerator per 100 pounds of the cement and the silica.
19. The cementitious composition of claim 13 , further comprising between 6 ounces and 32 ounces superplasticizer per 100 pounds of the cement and the silica.
20. The cementitious composition of claim 13 , further comprising at least one additive selected from a group consisting of a set accelerator, an air entraining agent, a finishing enhancer, a water reducer, a fumed microsilica, metakaolin, and a shrinkage reducer.
21. The cementitious composition of claim 13 , further comprising a dye.
22. A sheet of material, having a thickness of between 0.25 and 0.5 inch, comprising the cementitious composition of claim 13 .