Catalyst for purifying nitrogen oxides
View Patent ↗A catalyst for purifying NOx is provided which efficiently decomposes and purify the NOx in an exhaust gas in an oxygen-excess atmosphere, excels in resistance to heat and in durability in a high temperature range under a high-temperature oxidizing atmosphere and in the presence of moisture and SOx, and manifests the catalytic activity over a wide range of temperature. It is a catalyst for purifying nitrogen oxides formed by coating (A) a catalytically active component comprising (A-a) iridium and (A-b) at least one element selected from the group consisting of the elements of Group IIIA and Group IVA in the Periodic Table of the Elements with (B) a refractory inorganic compound.
1. A catalyst for purifying nitrogen oxides formed by coating (A) a catalytically active substance comprising (A-a) iridium, (A-b) tin and a powdered refractory inorganic oxide with (B) an aqueous slurry of refractory inorganic compound.
2. The catalyst for purifying nitrogen oxides according to claim 1 , wherein said catalyst is supported on a refractory inorganic substrate.
3. The catalyst for purifying nitrogen oxides according to claim 2 , wherein said refractory inorganic substrate is coated with a layer which contains a catalytically active substance comprising iridium (A-a), tin (A-b), and said powdered refractory inorganic oxide, and said layer is coated with a layer which contains the refractory inorganic compound (B).
4. The catalyst for purifying nitrogen oxide according to claim 1 , wherein said refractory inorganic compound (B) is at least one member selected from the group consisting of (B-a) a compound containing at least one member selected from the group consisting of aluminum, titanium, zirconium, and silicon, (B-b) a composite oxide thereof, (B-c) zeolite, and (B-d) barium sulfate.
5. The catalyst for purifying nitrogen oxides according to claim 1 , wherein said refractory inorganic compound (B) is zeolite and/or barium sulfate.
6. The catalyst for purifying nitrogen oxides according to claim 1 , wherein the molar ratio of tin (A-b) to iridium, [(A-b)/Ir], is in the range of 1:5 to 200:1 and the molar ratio of the refractory inorganic compound (B) to iridium, [(B)/Ir], is in the range of 10:1 to 100:1.
7. The catalyst for purifying nitrogen oxides according to claim 2 , wherein the amount of said powdered refractory inorganic oxide is in the range of 1 to 300 g per g of the refractory inorganic substrate.
8. The catalyst for purifying nitrogen oxides according to claim 1 , wherein the content of iridium is in the range of 0.1 to 20% by weight based on the amount of said powdered refractory inorganic oxide.
9. The catalyst for purifying nitrogen oxides according to claim 2 , wherein said catalyst is deposited in an amount in the range of 50 to 500 g per liter of the refractory inorganic substrate.