Non-aqueous borate routes to boron nitride
A non-aqueous route and process for preparation of boron nitride utilizing aerosol assisted vapor phase synthesis (AAVS) wherein boron precursors are nitrided in one or two heating steps, and wherein a boron oxide nitride carbide intermediary composition is formed after the first heating step and may be further nitrided to form resultant spheroidal boron nitride powders including dense or hollow spheroidal particles that are smooth, bladed, dense or hollow, have protruding whiskers, and are of turbostratic or hexagonal crystalline structure, specifically wherein the boron precursor is dissolved in a non-aqueous solution prior to aerosolization.
1. A plurality of hollow spherical particles comprising BN x O y C z , the hollow spherical particles being characterized by an average diameter of about 0.1 to about 10 microns and by a surface area of about 200 m 2 /g or more, and wherein x>0, y>0, and z>0.
2. The plurality of hollow spherical particles of claim 1 , wherein the hollow spherical particles are characterized by a surface area of about 1000 m 2 /g or more.
3. The plurality of hollow spherical particles of claim 1 , wherein the hollow spherical particles are characterized by a surface area about 200 m 2 /g to about 1500 m/g.
4. The plurality of hollow spherical particles of claim 1 , wherein the plurality of hollow spherical particles have an oxygen content of 15wt % or less.
5. The plurality of hollow spherical particles of claim 1 , wherein the plurality of hollow spherical particles have a carbon content of 0.5wt % or less.
6. The plurality of hollow spherical particles of claim 1 , wherein the plurality of hollow spherical particles are formed by the steps comprising:
dissolving boric acid in one member selected from the group consisting of N,N-dimethylformamide (DMF) and formamide to form a solution, wherein the solution comprises 20wt % or less of boric acid;
forming an aerosol from the solution;
using a gas stream to carry the aerosolized solution into a furnace; and
forming hollow BN x O y C z particles by injecting a gaseous nitriding agent into the furnace.
7. A plurality of hollow hexagonal crystal structure boron nitride particles (h-BN), the hollow hexagonal crystal structure boron nitride particles being characterized by an average diameter of about 1 to 10 microns and by a surface area of about 200 m 2 /g or more.
8. The plurality of hollow hexagonal crystal structure boron nitride particles of claim 7 , wherein the surface area is about 1000 m 2 /g or more.
9. The plurality of hollow hexagonal crystal structure boron nitride particles of claim 7 , wherein the surface area is about 200 m 2 /g to about 1500 m 2 /g.
10. The plurality of hollow hexagonal crystal structure boron nitride particles of claim 7 , wherein the plurality of hollow hexagonal crystal structure boron nitride particles are formed by the steps comprising:
dissolving boric acid in one member selected from the group consisting of N,N-dimethylformamide (DMF) and formamide to form a solution, wherein the solution comprises 20wt % or less of boric acid;
forming an aerosol from the solution;
using a gas stream to carry the aerosolized solution into a furnace; forming BN x O y C z particles by injecting a gaseous nitriding agent into the furnace; and
forming the plurality of hollow h-BN particles by heat treating the BN x O y C z particles in an atmosphere comprising the gaseous nitriding agent.