Interface engineering to improve adhesion between low k stacks
A method of depositing a organosilicate dielectric layer exhibiting high adhesion strength to an underlying substrate disposed within a single processing chamber without plasma arcing. The method includes positioning a substrate within a processing chamber having a powered electrode, flowing an interface gas mixture into the processing chamber, the interface gas mixture comprising one or more organosilicon compounds and one or more oxidizing gases, depositing a silicon oxide layer on the substrate by varying process conditions, wherein DC bias of the powered electrode varies less than 60 volts.
1. A method of depositing an organosilicate dielectric layer, comprising:
positioning a substrate within a processing chamber having a powered electrode;
flowing an interface gas mixture from a gas manifold into the processing chamber, the interface gas mixture comprising one or more organosilicon compounds and one or more oxidizing gases;
depositing a silicon oxide layer on the substrate by applying a high frequency radio frequency (HFRF) power to the powered electrode, the silicon oxide layer having a carbon concentration less than 3 atomic percent, wherein a distance between the substrate and the gas manifold is varied while applying HFRF power;
ramping-up the flow rate of the one or more organosilicon compounds until reaching a final gas mixture while depositing a transition layer on the silicon oxide layer, wherein a DC bias of the powered electrode varies less than 60 volts;
flowing the final gas mixture to deposit a carbon doped silicon oxide layer on the transition layer, the carbon doped silicon oxide layer having a carbon concentration of at least 10 atomic percent; and
terminating the HFRF power.
2. The method of claim 1 , wherein the ramping-up the flow rate of the one or more organosilicon compounds comprises gradually increasing the flow rate of the one or more organosilicon compounds at a ramp-up rate in a range of about 300 mg/min./sec. to about 900 mg/min./sec.
3. The method of claim 1 , wherein the silicon oxide layer comprises a carbon concentration less than 1 atomic percent.
4. The method of claim 1 , wherein the carbon doped silicon oxide layer comprises a carbon concentration greater than 20 atomic percent.
5. The method of claim 1 , further comprising applying a low frequency radio frequency (LFRF) power to the gas distribution manifold while depositing the carbon doped silicon oxide.
6. The method of claim 5 , further comprising ramping-up the LFRF power at a ramp-up rate in a range of about 15 W/sec to about 45 W/sec while depositing the transition layer.
7. The method of claim 1 , wherein the one or more organosilicon compounds comprises OMCTS.
8. The method of claim 1 , wherein the one or more oxidizing gases is oxygen and wherein the interface gas mixture comprises OMCTS and oxygen at a OMCTS:O 2 molar flow rate ratio of less than about 0.1.
9. The method of claim 1 , wherein the silicon oxide layer has a ratio of less than 0.001 Si—CH 3 or C—H bonds in comparison to Si—O bonds.
10. The method of claim 1 , wherein the silicon oxide layer is deposited with a final LFRF of about 80 to about 125 W.
11. A method of depositing a organosilicate dielectric layer, comprising:
positioning a substrate within a processing chamber having a gas distribution manifold;
flowing an interface gas mixture composition from a gas manifold into the processing chamber comprising helium, OMCTS, and one or more oxidizing gases;
depositing a silicon oxide layer on the substrate by applying a high frequency radio frequency (HFRF) power to the gas distribution manifold, the silicon oxide layer having a carbon concentration less than 3 atomic percent, wherein a distance between the substrate and the gas manifold is varied while applying HFRF power;
increasing the flow rate of the OMCTS at a ramp-up rate in a range of about 300 mg/min/sec to about 900 mg/min/sec until reaching a final gas mixture while depositing a transition layer on the interface layer;
flowing the final gas mixture to deposit a carbon doped silicon oxide layer on the transition layer, the carbon doped silicon oxide layer having a carbon concentration of at least 10 atomic percent; and
terminating the HFRF power.
12. The method of claim 11 , wherein DC bias of the gas distribution manifold varies less than 30 volts.
13. The method of claim 11 , wherein the ramping-up the flow rate of the one or more organosilicon compounds comprises increasing the flow rate of the OMCTS at a ramp rate of 600 mg/min/sec.
14. The method of claim 11 , wherein the silicon oxide layer comprises a carbon concentration less than 1 atomic percent.
15. The method of claim 11 , wherein the carbon doped silicon oxide layer comprises a carbon concentration greater than 20 atomic percent.
16. The method of claim 11 , further comprising applying a low frequency radio frequency (LFRF) power to the gas distribution manifold while depositing the carbon doped silicon oxide.
17. The method of claim 16 , further comprising ramping-up the LFRF power at a ramp-up rate in a range of about 15 W/sec to about 45 W/sec while depositing the transition layer.