Low and weakly-interlaced polyester multifilament yarn and method of producing the same
Disclosed is a low and weakly-interlaced industrial polyester multifilament yarn, which has excellent flatness and flat uniformity, and in which the number of monofilament layers is properly controlled according to a fineness of the low and weakly-interlaced polyester multifilament yarn and monofilaments are interlaced, thereby reducing a surface brightness gradient of a coated fabrics, produced using the low and weakly-interlaced polyester multifilament yarn, when light is irradiated to the coated fabrics. Additionally, the present invention provides a method of producing the low and weakly-interlaced polyester multifilament yarn, in which air pressure of an air interlacing device, a yarn path, tension of the yarn, an helix angle of the yarn wound around a cheese, intervals between first guides, located before and after the air interlacing device, and second guides, located in the air interlacing device, and a position of a wave plate are properly controlled.
1. A low and weakly-interlaced industrial polyester multifilament yarn with relatively high strength, wherein an average number of interlaced portions is 0.4 to 4.0 number/m, a deviation of the interlaced portions is 75 or less, an average thickness is 45 to 81 μm, an average tear strength of the interlaced portions is 3 to 15 gf, and a number of peaks, at which the average tear strength of the interlaced portions is 3 gf or more, is 8 peaks or less/5000 mm, wherein lengths of openings of the yarn are 5000 mm or less, wherein a winding angle of a yarn supplied to a winding cake (θ 1 ) is 160° or less leading to an increase of a tension of the yarn, and an interval length in an interlacing device is 50 cm or less so as to shorten wave length of yarn vibrations leading to a reduction of interlace portions of the yarn whereby enabling the yarn to be low and weakly interlaced.
2. The low and weakly-interlaced industrial polyester multifilament yarn as set forth in claim 1 , wherein a correlation of a fineness (D) and the average thickness (T) of the yarn is expressed as following equation:
T (μm) =c 3 D+c 4
wherein, 0.18≦c 3 ≦0.052 (c 3 is a constant) and 29≦c 4 ≦53 (c 4 is a thickness constant),
the most preferable average thickness being obtained from another equation, express as
T =0.36 D+ 40.32,
wherein a winding angle of a yarn supplied to a winding cake (θ 1 )is 160° or less leading to an increase of a tension of the yarn, and an interval length in an interlacing device is 50 cm or less so as to shorten wave length of yarn vibrations leading to a reduction of interlace portions of the yarn whereby enabling the yarn to be low and weakly interlaced.
3. A woven fabrics or knitted goods producing using the low and weakly-interfaced industrial polyester multifilament yarn according to claim 1 .
4. The woven fabrics or knitted goods as set forth in claim 3 , wherein the woven fabrics or knitted goods are coated with polyvinyl resins at a surface thereof.
5. A method of producing a low and weakly-interlaced polyester multifilament yarn with relative high strength, in which polyester multifilament is interlaced using an air interlacing device such that a tension is 0.06 to 0.18 g/d, air pressure is 1.00 to 1.40 kgf/cm 2 , an average number of interlaced portions is 0.4 to 4.0 number/m, comprising;
controlling intervals between first guides and second guides to 50 cm or less, the first guides being located before and after the air interlacing device, and the second guides being located in the air interlacing device, wherein a winding angle of a yarn supplied to a winding cake (θ 1 ) is 160° or less leading to an increase of a tension of the yarn, and an interval length in an interlacing device is 50 cm or less so as to shorten wave length of yarn vibrations leading to a reduction of interlace portions of the yarn whereby enabling the yarn to be low and weakly interlaced.