Process for reduction of inorganic contaminants from waste streams
The invention relates to the use of used alumina to reduce the level of inorganic contaminants, such as mercury and arsenic, from waste fluid streams. The invention further provides a process for reducing the level of mercury or arsenic in fluid streams by contacting the fluid stream with used alumina, such as used Claus catalyst.
1. A process for reducing the level of mercury from an aqueous liquid stream comprising contacting said liquid stream with a sulfur-bearing used Claus catalyst.
2. The process of claim 1 , wherein the used Claus catalyst has a sulfur concentration of 0.1-25% by weight.
3. The process of claim 2 , wherein the used Claus catalyst has a sulfur concentration of 0.1-2.0% by weight.
4. The process of claim 1 , wherein the used Claus catalyst is crushed prior to being loaded on the bed.
5. The process of claim 4 , wherein the used Claus catalyst is heated to remove moisture prior to being loaded on the bed.
6. The process of claim 1 , wherein at least about 50% of mercury is removed from said liquid stream.
7. The process of claim 1 , wherein at least about 75% of mercury is removed from said liquid stream.
8. The process of claim 1 , wherein at least about 90% of mercury is removed from said liquid stream.
9. The process of claim 1 , wherein the mercury is elemental mercury.
10. The process of claim 1 , wherein the mercury is ionic mercury.
11. A process for reducing the level of mercury from an aqueous liquid stream containing mercury, comprising the steps of
(a) flowing the liquid stream through a bed containing a sulfur-bearing used Claus catalyst sorbent;
(b) sorbing mercury from the liquid stream onto the surface of the sorbent; and
(c) allowing the mercury-depleted effluent stream to exit from the outlet of the bed.
12. The process of claim 11 , wherein the used Claus catalyst sorbent has a sulfur concentration of 0.1-25% by weight.
13. The process of claim 12 , wherein the used Claus catalyst sorbent has a sulfur concentration of 0.1-2.0% by weight.
14. The process of claim 11 , wherein the used Claus catalyst sorbent is crushed prior to being loaded on the bed.
15. The process of claim 14 , wherein the used Claus catalyst sorbent is heated to remove moisture prior to being loaded on the bed.
16. The process of claim 11 , wherein at least about 50% of mercury is removed from said liquid stream.
17. The process of claim 11 , wherein at least about 75% of mercury is removed from said liquid stream.
18. The process of claim 11 , wherein at least about 90% of mercury is removed from said liquid stream.
19. The process of claim 11 , wherein the mercury is elemental mercury.
20. The process of claim 11 , wherein the mercury is ionic mercury.