Waterborne hydrophobic barrier coatings
A waterborne hydrophobic barrier coating formulation comprising a blend of a vinyl acetate-ethylene (VAE) polymer emulsion and a paraffin wax emulsion, wherein a dried coating of the blend on a substrate, such as a nonwoven web, an absorbent pad, or a textile, and dried, has a hydrostatic head barrier sufficient to prevent passage of fluids but allow passage of water vapor through it. A multi-layer material comprising at least one layer of a nonwoven web, an absorbent pad, or a textile, and at least one layer of a blend of a VAE polymer emulsion and paraffin wax emulsion.
1. A blend comprising a poly(vinyl alcohol) stabilized vinyl acetate-ethylene polymer emulsion and a paraffin wax emulsion, wherein a dried coating of said blend on a substrate has a hydrostatic head barrier sufficient to prevent passage of fluids but allow passage of water vapor through it, the vinyl acetate-ethylene polymer emulsion comprises a polymer containing 70 to 95 wt % vinyl acetate and 5 to 30 wt % ethylene, based on the total weight of monomers in the polymer, and the paraffin wax in the paraffin wax emulsion has an average particle size of at least 0.3 microns.
2. The blend of claim 1 wherein the hydrostatic head barrier is at least 60 mm.
3. The blend of claim 2 wherein the vinyl acetate-ethylene polymer has a T g of 10 to 25° C.
4. The blend of claim 2 wherein the vinyl acetate-ethylene polymer emulsion has little or no formaldehyde and is free of alkylphenol ethoxylate surfactants.
5. The blend of claim 2 wherein the paraffin wax emulsion further comprises polyethylene or ethylene acrylic acid.
6. The blend of claim 2 comprising, on a 100% dry weight solids basis:
20-80%
vinyl acetate-ethylene polymer emulsion
20-80%
paraffin wax emulsion
0-10%
water soluble polymer or a protective colloid
0-3%
fluoro surfactant
0-5%
pigment.
7. The blend of claim 2 comprising, on a 100% dry weight solids basis:
40-60%
vinyl acetate-ethylene polymer emulsion
40-60%
paraffin wax emulsion
0-5%
water soluble polymer or a protective colloid
0-2%
fluoro surfactant
0-3%
pigment.