Electrically conductive diamond electrodes
View Patent ↗An electrically conductive diamond electrode and process for preparation thereof is described. The electrode comprises diamond particles coated with electrically conductive doped diamond preferably by chemical vapor deposition which are held together with a binder. The electrodes are useful for oxidation reduction in gas, such as hydrogen generation by electrolysis.
1. A process for the production of an electrically conductive diamond electrode which comprises:
(a) coating diamond particles with electrically conductive doped diamond to provide doped diamond particles comprising the diamond particles coated with the electrically conductive doped diamond; and
(b) binding the doped diamond particles with a binder so that the doped diamond particles are in electrical connection with each other to provide the diamond electrode.
2. The process of claim 1 wherein a portion of the doped diamond particles are exposed on at least one surface of the diamond electrode.
3. The process of claims 1 or 2 wherein individual doped diamond particles are in contact with each other in the binder so as to be conductive.
4. The process of claims 1 or 2 wherein the binder is electrically conductive along with the doped diamond particles.
5. The process of claims 1 or 2 wherein the doped diamond particles are coated with electrocatalytic particles.
6. The process of claims 1 or 2 wherein the doped diamond particles are coated with platinum metal particles.
7. The process of claims 1 or 2 wherein the doped diamond particles are coated with conductive metal particles.
8. The process of claim 7 , comprising coating the doped diamond particles with the conductive metal particles by electrodeposition.
9. The process of claims 1 or 2 wherein the electrically conductive doped diamond comprises a boron dopant.
10. The process of claims 1 or 2 wherein the doped diamond particles are coated with conductive metal particles and wherein the doped diamond particles with the conductive metal particles are coated with a film of chemical vapor deposited diamond to secure the conductive metal particles on the doped diamond particles.
11. The process of claim 10 wherein the chemical vapor deposition is accomplished by microwave assisted activation of deposition gases comprising an organic carbon source and hydrogen at reduced pressures.
12. The process of claim 1 wherein the diamond particles to be coated in step (a) comprise individual particles having a particle size ranging from about 0.1 μm to about 100 μm.
13. The process of claim 1 wherein the diamond particles to be coated in step (a) comprise individual particles having a particle size ranging from about 8 μm to about 12 μm.
14. The process of claim 1 wherein the diamond particles to be coated in step (a) have a specific surface area of at least about 2 m 2 /g.
15. The process of claim 1 wherein the diamond particles to be coated in step (a) have a specific surface area ranging from about 2 m 2 /g to about 5 m 2 /g.
16. The process of claim 1 , wherein coating the diamond particles in step (a) comprises performing chemical vapor deposition with sources gases comprising an organic carbon source gas, a hydrogen source gas, and a boron source gas, thereby forming the electrically conductive doped diamond.
17. The process of claim 1 , wherein coating the diamond particles in step (a) comprises performing chemical vapor deposition with sources gases comprising an organic carbon source gas, an argon source gas, and a boron source gas, thereby forming the electrically conductive doped diamond.