Antireflective transparent zeolite hardcoat, method for fabricating the same
View Patent ↗An antireflective transparent zeolite hardcoat and fabrication method thereof. The transparent zeolite hardcoat comprises a zeolite nanostructure made of zeolite nanocrystals vertically stacked into a porous structure on a substrate, wherein the porosity increases with structure height thereby providing a smooth refractive index transition. The hardcoat is deposited from a solution comprising the reaction products of a mixture via a two-stage thermal condensation process, wherein the mixture comprises a silica source, water and a zeolite structure directing agent.
1. A solution capable of forming an antireflective transparent zeolite hardcoat, comprising the reaction products of a mixture via a two-stage thermal condensation process, wherein the mixture comprises silica source, water, and zeolite structure directing agent (SDA), wherein the first stage thermal condensation process is performed at a temperature less than 100° C. for 13˜30 hours, and the second stage thermal condensation process is performed at a temperature between 150˜200° C. for 1˜2 hours, and the silica source is present in an amount of 20˜40 parts by weight, based on the 100 parts by weight of the mixture.
2. The solution as claimed in claim 1 , wherein the mixture further comprises a metal source and halide.
3. The solution as claimed in claim 1 , wherein the molar ratio between the zeolite structure directing agent and silica source is 0.2˜0.6.
4. The solution as claimed in claim 1 , wherein the silica source comprises C 1-2 alkyl orthosilicate.
5. The solution as claimed in claim 1 , wherein the zeolite structure directing agent comprises quatemary ammonium hydroxide or salts thereof.
6. The solution as claimed in claim 1 , wherein the silica source is ethyl orthosilicate and the zeolite structure directing agent is tetrapropylammonium hydroxide.