Treating metal surfaces with coating material
The present invention generally relates to an aqueous coating material with low VOC (Volatile Organic Compounds) and essentially zero HAP (Hazardous Air Pollutants) suitable for coating a metal surface, a method for treating metal, particularly steel, surfaces of a structure such as a joist with such aqueous coating material, and use of such aqueous coating material to treat metal surface to provide protection against corrosion particularly during delivery, storage on site, assembly, and erection in an atmosphere.
1. A method for treating a metal surface of a subject with an aqueous coating material comprising:
(A) providing the aqueous coating material;
(B) making an application of the aqueous coating material to the metal surface;
(C) removing any excess of the aqueous coating material from the subject; and
(D) drying the coated subject;
wherein the aqueous coating material comprises water, at least one resin, and at least one emulsifier or surfactant; wherein the resin comprises one or more polymerized C-5 and/or C-9 hydrocarbons and a liquid drying oil
wherein the resin is characterized by a density of from about 7.8 pounds per gallon (0.936 kg per liter) to about 8.2 pounds per gallon (0.984 kg per liter), a Gardner Color of 3− to 9+, less than 1% volatile matter after 2 hours @ 100° C., and a viscosity of 600-1700 centipoise wherein said viscosity is measured @ 25° C.; and
the aqueous coating material is characterized by a solids content in the range of from about 50% to about 70% by weight, from about 35% to about 55% by volume; a VOC content of not more than 120 grams per liter excluding water; and a viscosity in the range of from about 20 to about 55 centipoise.
2. The method of claim 1 , wherein the application is dipping.
3. The method of claim 2 , wherein the metal is steel.
4. The method of claim 3 , wherein the subject is a joist and the application is dipping.
5. The method of claim 1 , wherein the aqueous coating material further comprises one or more components selected from the group consisting of a biocide, an adhesion promoter, a corrosion inhibitor, a wetting agent, and mixtures thereof.
6. The method of claim 1 , wherein the solids content is in the range of from about 55% to about 65% by weight, the VOC content is less than 113 grams per liter excluding water, and the viscosity is in the range of from about 25 to about 35 centipoise.
7. The method of claim 6 , wherein the application comprises dipping.
8. The method of claim 7 , wherein the metal is steel.
9. The method of claim 8 , wherein the metal is a steel joist.
10. A method for treating a steel surface of a joist with an aqueous coating material comprising:
(A) providing the aqueous coating material;
(B) dipping the joist into a vat containing the aqueous coating material;
(C) removing any excess of the aqueous coating material from the joist; and
(D) drying;
wherein the aqueous coating material comprises water, at least one resin, and at least one fatty ester emulsifier or one fatty acid surfactant;
the resin comprises one or more polymerized C-5 and/or C-9 hydrocarbons and a liquid drying oil containing at least one copolymer containing one monomer with at least one diallylic group and at least 50% of one or more di-unsaturated acids, 35% of one or more mono-unsaturated acids; and,
said resin is characterized by a density of about 7.8 pounds per gallon (0.936 kg per liter) to about 8.2 pounds per gallon (0.984 kg per liter), a Gardner Color of 3−9+, less than 1% volatile matter after 2 hours @ 100° C., and a viscosity of 600-1700 centipoise, said centipoise measured @ 25° C.;
and the aqueous coating material is characterized by a solids content in the range of from about 55% to about 65% by weight, from about 40% to about 50% by volume;
a VOC content of not more than 113 grams per liter excluding water;
a viscosity in the range of from about 20 to about 55 centipoise; and the joist carrying said dried aqueous coating material exhibits 100 or more hours of salt spray resistance as measured by the testing method ASTMB-117.
11. A method for treating the surface of a metal object with an aqueous coating material comprising:
(A) providing the aqueous coating material;
(B) applying the aqueous coating material to the surface of said metal object;
(C) removing any excess aqueous coating material from the said metal object; and
(D) drying the coating material on the surface of the metal object thereby yielding a metal object having a coating of said aqueous coating material;
wherein the aqueous coating material comprises water, at least one resin, and at least one emulsifier or surfactant; wherein the resin comprises one or more polymerized C-5 and/or C-9 hydrocarbons and a liquid drying oil, said resin having a viscosity of 600-1700 centipoise when said viscosity is measured @ 25° C.; and
the aqueous coating material has a solids content in the range of from about 50% to about 70% by weight, a VOC content of not more than 120 grams per liter excluding water; and a viscosity in the range of from about 20 to about 55 centipoise.
12. The method of claim 11 , wherein said step of applying said aqueous coating material to said metal object entails dipping said metal object into a container of said aqueous coating material.
13. The method of claim 11 , wherein the aqueous coating material further comprises one or more components selected from the group consisting of a biocide, an adhesion promoter, a corrosion inhibitor, a wetting agent, and mixtures thereof.
14. The method of claim 11 , wherein said metal object is a steel joist.