Polyamide fiber for uncoated airbags
A high strength polyamide fiber consisting of polyamide monofilaments each having a fineness of less than 4 denier and a stress-strain curve where (a) the monofilament elongates less than 5% when subjected to an initial stress of 1.0 g/d, (b) it elongates less than 12% when subjected to a middle stress of 4.5 g/d, and (c) it elongates more than 3% over a tensile strength range from a tensile strength of at least 9.0 d/g to the tensile strength at break of the monofilament, the elongation values being measured at ambient temperature.
1. An airbag constructed of a fabric woven from a polyamide monofilament produced by a process of:
(A) melt-spinning polyhexamethyleneadipamide polymer at a spinning draft ratio of 20-200 with a residual time of the polymer adjusted to 3-30 seconds to thereby prepare the undrawn yarn having a fineness of 10 to 25; and (B) a multi-stage drawing process where the second drawing ratio is higher than the first drawing ratio and the third drawing ratio is lower than the second,
wherein the polyamide monofilament has a fineness of less than 4 denier and a stress-strain curve where (a) the polyamide monofilament elongates less than 5% when subjected to an initial stress of 1.0 g/d, (b) it elongates less than 12% when subjected to a middle stress of 4.5 g/d, and (c) it elongates more than 3% over a tensile strength range from a tensile strength of at least 9.0 g/d to the tensile strength at break of the monofilament yarn, the elongation values being measured at ambient temperature, wherein the (a), (b) and (c) is adjusted within the above range for absorbing impact energy occurring instantaneously when the airbag operates.
2. The airbag of claim 1 , in which the polyamide monofilament has a tensile strength at break of 9.0-11 g/d.
3. The airbag of claim 1 , in which the polyamide monofilament has a fineness of 2-3.5 denier.
4. An airbag constructed of a fabric woven from an assembly of the polyamide monofilaments of claim 1 .
5. The airbag of claim 4 , wherein the number of the polyamide monofilaments in the polyamide monofilament assembly is 50-500.
6. The airbag of claim 4 , wherein the number of the polyamide monofilaments in the polyamide monofilament assembly is 136.
7. The airbag of claim 4 , which has a total fineness of 200-800 denier.
8. The airbag of claim 1 , wherein the fabric has a tensile strength of 200-300 kg.
9. The airbag of claim 1 , wherein the fabric has a tear strength of 25-40 kg.
10. The airbag of claim 1 , wherein the fabric has an air permeability of less than 1.0 cm 3 /cm 2 /sec.