Flexible monolayer elastomer films and bag for medical use
Soft, flexible films suitable for human skin contact are required for disposable medical devices. Soft, flexible monolayer elastomer films have been developed that are suitable for human skin contact and provide improved low-temperature flexibility and improved strength to weight ratio over conventional polyvinyl chloride films for medical uses. Embodiments of the flexible monolayer elastomer film include styrene-ethylene-propylene-styrene block copolymers (SEPS), SEPS/polyolefin mixtures, SEPS/polyolefin/ethylene-vinyl acetate (EVA) copolymer mixtures, and EVA/polyolefin mixtures.
1. A flexible monolayer elastomer film consisting essentially of from about 55% to about 75% by weight of an ethylene-vinyl acetate copolymer and from about 25% to about 45% by weight of a metallocene catalyzed ethylene-octene copolymer, the film having a texture, the texture being substantially that of plasticized polyvinyl chloride, and wherein the film is essentially free of leachable material.
2. A flexible monolayer bag for storing medical products, wherein the bag is formed from the flexible monolayer elastomer film of claim 1 .
3. The flexible monolayer elastomer film of claim 1 , wherein the film has an oxygen transmission rate of from about 100 cm 3 /100 in 2 /24 hours to about 600 cm 3 /100 in 2 /24 hours, a carbon dioxide transmission rate of from about 1000 cm 3 /100 in 2 /24 hours to about 5000 cm 3 /100 in 2 /24 hours, and a water vapor transmission rate of from about 1.7 g/100 in 2 /24 hours to about 2.7 g/100 in 2 /24 hours; for 0.006″ thick films.
4. The flexible monolayer elastomer film of claim 1 , wherein the film has an oxygen transmission rate of from about 300 cm 3 /100 in 2 /24 hours to about 400 cm 3 /100 in 2 /24 hours and a carbon dioxide transmission rate of from about 2500 cm 3 /100 in 2 /24 hours to about 3500 cm 3 /100 in 2 /24 hours; for 0.006″ thick films.
5. A flexible monolayer elastomer film consisting essentially of from about 55% to about 75% by weight of an ethylene-vinyl acetate copolymer, from about 25% to about 45% by weight of a metallocene catalyzed ethylene-octene copolymer, and optionally 5% to 20% by weight of one or more of a styrene-ethylene-propylene-styrene block copolymer, a syndiotactic polypropylene, a polypropylene homopolymer, a polypropylene copolymer, a metallocene catalyzed isotactic polypropylene, a low-density polyethylene, and a linear low-density polyethylene, the film having a texture, the texture being substantially that of plasticized polyvinyl chloride, and wherein the film is essentially free of leachable material.
6. A flexible monolayer bag for storing medical products, wherein the bag is formed from the flexible monolayer elastomer film of claim 5 .
7. The flexible monolayer elastomer film of claim 5 , wherein the film has an oxygen transmission rate of from about 100 cm 3 /100 in 2 /24 hours to about 600 cm 3 /100 in 2 /24 hours, a carbon dioxide transmission rate of from about 1000 cm 3 /100 in 2 /24 hours to about 5000 cm 3 /100 in 2 /24 hours, and a water vapor transmission rate of from about 1.7 g/100 in 2 /24 hours to about 2.7 g/100 in 2 /24 hours; for 0.006″ thick films.
8. The flexible monolayer elastomer film of claim 5 , wherein the film has an oxygen transmission rate of from about 300 cm 3 /100 in 2 /24 hours to about 400 cm 3 /100 in 2 /24 hours and a carbon dioxide transmission rate of from about 2500 cm 3 /100 in 2 /24 hours to about 3500 cm 3 /100 in 2 /24 hours; for 0.006″ thick films.