High density cobalt-manganese coprecipitated nickel hydroxide and process for its production
The present invention provides high density cobalt-manganese coprecipitated nickel hydroxide, particularly having a tapping density of 1.5 g/cc or greater, and a process for its production characterized by continuous supply of an aqueous solution of a nickel salt which contains a cobalt salt and a manganese salt, of a complexing agent and of an alkali metal hydroxide, into a reactor either in an inert gas atmosphere or in the presence of a reducing agent, continuous crystal growth and continuous removal.
1. Spherical particles of high density cobalt-manganese coprecipitated nickel hydroxide for the production of the positive electrode active material of a lithium ion secondary battery that are free of non-spherical particles of the same; wherein said cobalt-manganese coprecipitated nickel hydroxide is represented by the formula:
(Ni (1-x-y) Co x Mn y )(OH) 2
wherein 1/10≦x≦⅓ and 1/20≦y≦⅓; and
wherein said particles have a tapping density of 1.5 g/cc or greater and a mean particle size in the range of 5-20 μm.
2. Spherical particles of high density cobalt-manganese coprecipitated nickel hydroxide for the production of the positive electrode active material of a lithium ion secondary battery that are free of non-spherical particles of the same, wherein said particles have a tapping density of 1.5 g/cc or greater and a mean particle size in the range of 5-20 μm, wherein said cobalt-manganese coprecipitated nickel hydroxide is represented by the formula:
(Ni (1-x-y) Co x Mn y )(OH) 2
wherein 1/10≦x≦⅓ and 1/20≦y≦⅓;
prepared by a process comprising the steps of:
continuously supplying an aqueous solution of a nickel salt which contains a cobalt salt and a manganese salt of a complexing agent and an alkali metal hydroxide into a reactor either in an inert gas atmosphere or in the presence of a reducing agent;
continuously growing crystals of said particles; and
continuously removing crystals of said particles from said reactor.
3. The spherical particles of claim 2 , wherein said reducing agent is hydrazine.
4. A process for production of high density cobalt-manganese coprecipitated nickel hydroxide of claim 1 , comprising the steps of:
continuously supplying an aqueous solution of a nickel salt which contains a cobalt salt and a manganese salt, a complexing agent, and an alkali metal hydroxide into a reactor either in an inert gas atmosphere or in the presence of a reducing agent;
continuously growing crystals of said particles; and
continuously removing crystals of said particles from said reactor.
5. The process of claim 4 wherein said reducing agent is hydrazine.
6. The process of claim 4 , wherein the salt concentration in said reactor is kept in a range of 50-200 mS/cm±5 mS/cm, wherein the ammonium ion concentration is kept in a range of 1-10 g/L±0.5 g/L, wherein the reaction pH is kept in a range of 11.0-13.0±0.05, wherein the reaction temperature is kept at 25-80° C.±0.5° C.
7. The spherical particles of claim 1 , wherein said particles have a surface area of 8 to 20 m 2 /g.
8. The spherical particles of claim 2 , wherein said particles have a surface area of 8 to 20 m 2 /g.
9. The process of claim 4 , wherein said complexing agent is a source of ammonium ion.
10. The spherical particles of claim 2 , wherein said complexing agent is a source of ammonium ion.