A family of glasses from the rare earth alumino-silicate (RE 2 O 3 —Al 2 O 3 —SiO 2 ) ternary system exhibiting high strain point and low liquidus temperatures; preferably the La 2 O 3 —Al 2 O 3 —SiO 2 ternary system. The glasses are excellent candidates for electronics applications and have the following composition, expressed in mole percent and calculated from the glass batch on an oxide basis: 60-85% SiO 2 , 10-25% Al 2 O 3 , and 4-15% RE 2 O 3 .
1. A substrate for a flat panel display device comprising a rare earth aluminosilicate glass exhibiting a strain point greater than approximately 650° C., a liquidus temperature less than approximately 1300° C., the glass comprising the following composition when calculated in mole percent and calculated from the batch on an oxide basis:
60-75%SiO 2
10.6-20% Al 2 O 3
2-15%RE 2 O 3
the RE being a rare earth selected from group consisting of Sc, Y, La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu and mixtures thereof; and
1-12% of one or more RO, wherein R is an alkaline earth metal selected from the group consisting of Mg, Ca, Sr, or any combination thereof; or when R is Ba, at least one additional alkaline earth metal selected from the group consisting of Mg, Ca, and Sr is present;
0-9% B 2 O 3 ; and
0-2% SnO 2 ,
wherein the composition does not contain TiO 2 and Ta 2 O 5 either individually or in any combination thereof.
2. The substrate of claim 1 wherein said substrate comprises the following composition when calculated in mole percent and calculated from the batch on an oxide basis:
65-75% SiO 2
10.6-20% Al 2 O 3
4-15% RE 2 O 3 .
3. The substrate of claim 1 having a strain point of at least 650° C.
4. The substrate of claim 1 wherein the substrate comprises, in mole percent and calculated from the batch on an oxide basis, 2-15% La 2 O 3 .
5. The substrate of claim 1 having a liquidus temperature of no greater than 1300° C.
6. The substrate of claim 1 having a liquidus viscosity greater than 10,000 poise.
7. A rare earth aluminosilicate glass exhibiting a strain point greater than approximately 650° C., a liquidus temperature less than approximately 1300° C., the glass comprising the following composition as calculated in a mole percent on an oxide basis:
65-75% SiO 2
10.6-20% Al 2 O 3
2-15% RE 2 O 3
the RE being a rare earth selected from the group consisting of Sc, Y, La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu, and mixtures thereof; and
1-12% of one or more RO, wherein R is an alkaline earth metal selected from the group consisting of Mg, Ca, r, or any combination thereof; or when R is Ba, at least one additional alkaline earth metal selected from the group consisting of Mg, Ca, and Sr is presented;
0-9% B 2 O 3 ; and
0-2% SnO 2 ,
wherein the composition does not contain TiO 2 and Ta 2 O 5 either individually or in any combination thereof.
8. The glass of claim 7 further exhibiting a liquidus viscosity of greater than 10,000 poise.
9. The glass of claim 7 further exhibiting a 200 Poise temperature that is less than 1550° C.
10. The glass of claim 7 , wherein the glass is a substrate present in an electronic device.
11. The glass of claim 10 wherein the electronic device is an LCD display.
12. The glass of claim 7 , wherein Re is La.
13. The glass of claim 7 , wherein RE is La, and the amount of La 2 O 3 is from 2-12.49% in mole percent as calculated from the batch on an oxide basis.
14. The glass of claim 7 , wherein the amount of RO is about 7-12% mole percent as calculated from the batch on an oxide basis.
15. The glass of claim 7 , wherein the amount of RO is about 10-12% mole percent as calculated from the batch on an oxide basis.
16. The glass of claim 7 , wherein the amount of B 2 O 3 is about 0-3% mole percent as calculated from the batch on an oxide basis.
17. The glass of claim 7 , wherein the glass has a coefficient of thermal expansion (0-300° C.) of 25-50×10 −7 /° C.
18. The glass of claim 7 , wherein the glass has liquidus temperature less than 1250° C.
19. The glass of claim 7 , further comprising a ratio (RO+1.5*RE 2 O 3 )/Al 2 O 3 wherein the ratio is between 0.85 and 1.2.
20. A rare earth aluminosilicate glass exhibiting a strain point greater than approximately 650° C., a liquidus temperature less than approximately 1300° C., the glass consisting of the following composition as calculated in a mole percent on an oxide basis:
60-75% SiO 2
10-20% Al 2 O 3
2-12.49% RE 2 O 3
the RE being a rare earth selected from the group consisting of Sc, Y, La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu, and mixtures thereof; and
1-12% of one or more RO, wherein R is an alkaline earth metal selected from the group consisting of Mg, Ca, and Sr; or when R is Ba, at least one additional alkaline earth metal, selected from the group consisting of Mg, Ca, and Sr is present;
0-9% B 2 O 3 ; and
0-2% SnO 2 .
21. The glass of claim 20 , wherein the glass is a substrate present in an electronic device.
22. The glass of claim 21 , wherein the electronic device is an LCD display.
23. The lass of claim 20 , further comprising a 200 Poise temperature that is less than 1550° C.