Fiber reinforced filter for molten metal filtration
The present invention relates to a fiber reinforced ceramic filter for molten metal filtration that comprises a bonded network of graphitized carbon and a method for producing such filters.
1. A ceramic filter for molten metal filtration comprising a ceramic powder and fibers bonded by a network of graphitizable carbon fired in a non-oxidizing atmosphere at a temperature from 500° C. to 1000° C., wherein the graphitizable carbon is produced from graphitizable carbon precursor present in an amount from 2% to 15% by weight.
2. The filter of claim 1 , wherein the ceramic powder is selected from a group consisting of zirconia, silica, alumina, brown fused alumina, magnesia, clay, talcum, mica, silicon carbide, silicon-nitride, graphite and mixtures thereof.
3. The filter of claim 1 , wherein the filter comprises graphitizable carbon produced from 5 to 15 wt % graphitizable carbon precursor, and wherein the graphitizable carbon is fired in a non-oxidizing atmosphere at a temperature from 500° C. to 1000° C.
4. The filter of claim 1 , wherein the fibers are selected from a group consisting of ceramic fibers, glass fibers, organic fibers, carbon fibers, metal fibers and mixtures thereof.
5. The filter of claim 1 , wherein the filter comprises 1-10 wt % fibers.
6. A filter for molten metal filtration comprising fibers bonded by a network of graphitizable carbon fired in a non-oxidizing atmosphere at a temperature from 500° C. to 1000° C., wherein the graphitizable carbon is produced from graphitizable carbon precursor present in an amount from 2% to 15% by weight.
7. The filter of claim 6 , wherein the fibers are selected from a group consisting of ceramic fibers, glass fibers, organic fibers, carbon fibers, metal fibers and mixtures thereof.
8. The filter of claim 7 , wherein the ceramic fibers are selected from a group consisting of alumina fibers, silica fibers, aluminosilicate fibers and mixtures thereof.
9. The filter of claim 7 , wherein the organic fibers are selected from a group consisting of polyester fibers, polyacrylnitrile fibers, polyethylene fibers, polyamide fibers, viscose fibers, aramid fibers and mixtures thereof.
10. The filter of claim 6 , wherein the filter comprises 1-10 wt % fibers.
11. The filter of claim 6 , wherein the fibers have a length from 0.1 to 5 mm.