Antifouling condensation curing organopolysiloxane composition and underwater structure
An anti-fouling condensation curing organopolysiloxane composition is provided comprising in admixture, (A) 100 parts by weight of a base polymer in the form of a diorganopolysiloxane having at least two silicon atom-bonded hydroxyl or hydrolyzable groups in a molecule, at least 2 mol % of entire substituent groups being phenyl groups, (B) 0.5 to 30 parts by weight of a silane having at least two hydrolyzable groups or a partial hydrolytic condensate thereof, and (C) 5 to 100 parts by weight of a non-reactive dialkylpolysiloxane. The composition cures at room temperature to form a coating which is non-toxic, non-detrimental to the environment, and effective for preventing aquatic organisms from depositing and growing thereon over a long term.
1. An anti-fouling condensation curing organopolysiloxane composition comprising in admixture,
(A) 100 parts by weight of a base polymer in the form of a diorganopolysiloxane having at least two silicon atom-bonded hydroxyl or hydrolyzable groups in a molecule, in which 8 to 25 mol % of entire substituent groups bonded to silicon atoms are phenyl groups, wherein said diorganopolysiloxane has a viscosity at 25° C. of 1000 to 2000 mm 2 /s,
(B) 0.5 to 30 parts by weight of a silane having at least two hydrolyzable groups in a molecule and/or a partial hydrolytic condensate thereof, and
(C) 5 to 100 parts by weight of a diorganopolysiloxane having the general formula (4):
wherein R 2 is methyl and/or ethyl, X is an oxygen atom or a divalent hydrocarbon group of 1 to 8 carbon atoms, and the subscript n is a number such that the diorganopolysiloxane has a viscosity of 100 to 1000 at mm 2 /s at 25° C., provided that the ratio of the viscosity of component (C) to the viscosity of component (A) is in a range of 0.02 to 0.8, and
(D) 5 to 100 parts by weight of hydrophilic silica having a BET specific surface area of at least 10 m 2 /g as a filler.
2. The composition of claim 1 , wherein said base polymer (A) is a diorganopolysiloxane having the general formula (1) and/or (2):
wherein R is a substituted or unsubstituted monovalent hydrocarbon group, at least 2 mol % of R being phenyl groups, X is an oxygen atom or a divalent hydrocarbon group of 1 to 8 carbon atoms, and n is such a number that the diorganopolysiloxane has a viscosity of 1000 to 2000 mm 2 /s at 25° C.,
wherein R is a substituted or unsubstituted monovalent hydrocarbon group, at least 2 mol % of R being phenyl groups, X is an oxygen atom or a divalent hydrocarbon group of 1 to 8 carbon atoms, Y is a hydrolyzable group, “a” is equal to 2 or 3, and n is such a number that the diorganopolysiloxane has a viscosity of 1000 to 2000 mm 2 /s at 25° C.
3. The composition of claim 1 , wherein component (B) is a silane of the general formula (3):
R 1 b SiZ 4-b (3)
wherein R 1 is each independently a substituted or unsubstituted monovalent hydrocarbon group of 1 to 6 carbon atoms, Z is each independently a hydrolyzable group, and b is an integer of 0 to 2, and/or a partial hydrolytic condensate thereof.
4. The composition of claim 1 , wherein component (C) is dimethylpolysiloxane.
5. The composition of claim 1 , further comprising a filler selected from among calcium carbonate, calcium silicate and silica zeolite.
6. The composition of claim 1 , wherein the ratio in viscosity of diorganopolysiloxane (C) to diorganopolysiloxane (A) is from 0.05 to 0.7.
7. An underwater structure coated with a cured product of an anti-fouling condensation curing organopolysiloxane composition comprising in admixture,
(A) 100 parts by weight of a base polymer in the form of a diorganopolysiloxane having at least two silicon atom-bonded hydroxyl or hydrolyzable groups in a molecule, in which 8 to 25 mol % of entire substituent groups bonded to silicon atoms are phenyl groups, wherein said diorganopolysiloxane has a viscosity at 25° C. of 1000 to 2000 mm 2 /s,
(B) 0.5 to 30 parts by weight of a silane having at least two hydrolyzable groups in a molecule and/or a partial hydrolytic condensate thereof, and
(C) 5 to 100 parts by weight of a diorganopolysiloxane having the general formula (4):
wherein R 2 is methyl and/or ethyl, X is an oxygen atom or a divalent hydrocarbon group of 1 to 8 carbon atoms, and the subscript n is a number such that the diorganopolysiloxane has a viscosity of 100 to 1000 mm 2 /s at 25° C., provided that the ratio of the viscosity of component (C) to the viscosity of component (A) is in a range of 0.02 to 0.8, and
(D) 5 to 100 parts by weight of hydrophilic silica having a BET specific surface area of at least 10 m 2 /g as a filler.
8. The underwater structure of claim 7 , wherein said base polymer (A) is a diorganopolysiloxane having the general formula (1) and/or (2):
wherein R is a substituted or unsubstituted monovalent hydrocarbon group, at least 2 mol % of R being phenyl groups, X is an oxygen atom or a divalent hydrocarbon group of 1 to 8 carbon atoms, and n is such a number that the diorganopolysiloxane has a viscosity of 1000 to 2000 mm 2 /s at 25° C.,
wherein R is a substituted or unsubstituted monovalent hydrocarbon group, at least 2 mol % of R being phenyl groups, X is an oxygen atom or a divalent hydrocarbon group of 1 to 8 carbon atoms, Y is a hydrolyzable group, “a” is equal to 2 or 3, and n is such a number that the diorganopolysiloxane has a viscosity of 1000 to 2000 mm 2 /s at 25° C.
9. The underwater structure of claim 7 , wherein component (B) is a silane of the general formula (3):
R 1 b SiZ 4-b (3)
wherein R 1 is each independently a substituted or unsubstituted monovalent hydrocarbon group of 1 to 6 carbon atoms, Z is each independently a hydrolyzable group, and b is an integer of 0 to 2, and/or a partial hydrolytic condensate thereof.
10. The underwater structure of claim 7 , wherein component (C) is dimethylpolysiloxane.
11. The underwater structure of claim 7 , further comprising a filler selected from among calcium carbonate, calcium silicate, and silica zeolite.
12. An anti-fouling condensation curing organopolysiloxane composition comprising in admixture,
(A) 100 parts by weight of a base polymer in the form of a diorganopolysiloxane having at least two silicon atom-bonded hydroxyl or hydrolyzable groups in a molecule, in which 8 to 25 mol % of entire substituent groups bonded to silicon atoms are phenyl groups, wherein said diorganopolysiloxane has a viscosity at 25° C. of 10,000 to 30,000 mm 2 /s,
(B) 0.5 to 30 parts by weight of a silane having at least two hydrolyzable groups in a molecule and/or a partial hydrolytic condensate thereof, and
(C) 5 to 100 parts by weight of a diorganopolysiloxane having the general formula (4):
wherein R 2 is methyl and/or ethyl, X is an oxygen atom or a divalent hydrocarbon group of 1 to 8 carbon atoms, and the subscript n is a number such that the diorganopolysiloxane has a viscosity of 1000 to 5000 mm 2 /s at 25° C., provided that the ratio of the viscosity of component (C) to the viscosity of component (A) is in a range of 0.02 to 0.8, and
(D) 5 to 100 parts by weight of hydrophilic silica having a BET specific surface area of at least 10 m 2 /g as a filler.
13. The composition of claim 12 , wherein said base polymer (A) is a diorganopolysiloxane having the general formula (1) and/or (2):
wherein R is a substituted or unsubstituted monovalent hydrocarbon group, at least 2 mol % of R being phenyl groups, X is an oxygen atom or a divalent hydrocarbon group of 1 to 8 carbon atoms, and n is such a number that the diorganopolysiloxane has a viscosity of 10,000 to 30,000 mm 2 /s at 25° C.,
wherein R is a substituted or unsubstituted monovalent hydrocarbon group, at least 2 mol % of R being phenyl groups, X is an oxygen atom or a divalent hydrocarbon group of 1 to 8 carbon atoms, Y is a hydrolyzable group, “a” is equal to 2 or 3, and n is such a number that the diorganopolysiloxane has a viscosity of 10,000 to 30,000 mm 2 /s at 25° C.
14. The composition of claim 12 , wherein component (B) is a silane of the general formula (3):
R 1 b SiZ 4-b (3)
wherein R 1 is each independently a substituted or unsubstituted monovalent hydrocarbon group of 1 to 6 carbon atoms, Z is each independently a hydrolyzable group, and b is an integer of 0 to 2, and/or a partial hydrolytic condensate thereof.
15. The composition of claim 12 , wherein component (C) is dimethylpolysiloxane.
16. The composition of claim 12 , further comprising a filler selected from among calcium carbonate, calcium silicate and silica zeolite.
17. The composition of claim 12 , wherein the ratio in viscosity of diorganopolysiloxane (C) to diorganopolysiloxane (A) is from 0.05 to 0.7.
18. An underwater structure coated with a cured product of an anti-fouling condensation curing organopolysiloxane composition comprising in admixture,
(A) 100 parts by weight of a base polymer in the form of a diorganopolysiloxane having at least two silicon atom-bonded hydroxyl or hydrolyzable groups in a molecule, in which 8 to 25 mol % of entire substituent groups bonded to silicon atoms are phenyl groups, wherein said diorganopolysiloxane has a viscosity at 25° C. of 10,000 to 30,000 mm 2 /s,
(B) 0.5 to 30 parts by weight of a silane having at least two hydrolyzable groups in a molecule and/or a partial hydrolytic condensate thereof, and
(C) 5 to 100 parts by weight of a diorganopolysiloxane having the general formula (4):
wherein R 2 is methyl and/or ethyl, X is an oxygen atom or a divalent hydrocarbon group of 1 to 8 carbon atoms, and the subscript n is a number such that the diorganopolysiloxane has a viscosity of 1000 to 5000 mm 2 /s at 25° C., provided that the ratio of the viscosity of component (C) to the viscosity of component (A) is in a range of 0.02 to 0.8, and
(D) 5 to 100 parts by weight of hydrophilic silica having a BET specific surface area of at least 10 m 2 /g as a filler.
19. The underwater structure of claim 18 , wherein said base polymer (A) is a diorganopolysiloxane having the general formula (1) and/or (2):
wherein R is a substituted or unsubstituted monovalent hydrocarbon group, at least 2 mol % of R being phenyl groups, X is an oxygen atom or a divalent hydrocarbon group of 1 to 8 carbon atoms, and n is such a number that the diorganopolysiloxane has a viscosity of 10,000 to 30,000 mm 2 /s at 25° C.,
wherein R is a substituted or unsubstituted monovalent hydrocarbon group, at least 2 mol % of R being phenyl groups, X is an oxygen atom or a divalent hydrocarbon group of 1 to 8 carbon atoms, Y is a hydrolyzable group, “a” is equal to 2 or 3, and n is such a number that the diorganopolysiloxane has a viscosity of 10,000 to 30,000 mm 2 /s at 25° C.
20. The underwater structure of claim 18 , wherein component (B) is a silane of the general formula (3):
R 1 b SiZ 4-b (3)
wherein R 1 is each independently a substituted or unsubstituted monovalent hydrocarbon group of 1 to 6 carbon atoms, Z is each independently a hydrolyzable group, and b is an integer of 0 to 2, and/or a partial hydrolytic condensate thereof.
21. The underwater structure of claim 18 , wherein component (C) is dimethylpolysiloxane.
22. The underwater structure of claim 18 , further comprising a filler selected from among calcium carbonate, calcium silicate, and silica zeolite.