Medical adsorbent and process for production of the same
View Patent ↗A medical adsorbent which produces minimal side-effects such as constipation, has excellent adsorption for ionic organic compounds such as causative substances of uremia, exhibits adequate adsorption performance at low doses and avoids adsorption of high-molecular compounds necessary for the body, such as enzymes and polysaccharides. The medical adsorbent comprises activated carbon obtained by carbonizing a spherical phenol resin in a nitrogen atmosphere at a temperature of 400-1000° C., activating the carbonized spherical phenol resin at a temperature of 800-1000° C., washing it with dilute hydrochloric acid, heat treating it at a temperature of 150-1000° C. in a mixed gas comprising oxygen and nitrogen and then sorting it; the activated carbon has an area to weight ratio of 500-2000 m 2 /g, a pore volume of 0.2-1.0 mL/g and a packing density of 0.5-0.75 g/mL.
1. A medical adsorbent comprising spherical activated carbon which is activated carbon obtained by carbonizing and activating a spherical phenol resin and which has (a) an area to weight ratio of 800-2000 m 2 /g, (b) a pore volume of 0.2-1.0 mL/g, (c) a packing density of 0.5-0.75 g/mL, (d) a mean pore diameter of 1.7-2.0 nm, (e) a maximum particle size of no greater than 425 μm and a mean particle size of no greater than 350 μm, and (f) an overall pore volume of no greater than 0.04 mL/g of pores with pore diameters of 20-1000 nm, wherein the overall pore volume of pores with a mean pore diameter of no greater than 1.0 nm constitutes at least 55% of the total pore volume.
2. A medical adsorbent according to claim 1 , wherein said spherical activated carbon has a surface oxide content of at least 0.35 meq/g.
3. A medical adsorbent according to claim 1 , wherein the difference between the proportions of particles of no larger than 103 μm before and after powdering of said spherical activated carbon is no greater than 5%.
4. A process for production of a medical absorbent according to any one of claims 1 , 2 , and 3 , which process comprises:
a step of carbonizing a spherical phenol resin in a nitrogen atmosphere at a temperature of 400-1000° C.,
a step of activating the carbonized spherical phenol resin at a temperature of 800-1000° C.,
a step of washing the activated spherical phenol resin with dilute hydrochloric acid,
a step of heat treatment at a temperature of 150-1000° C. in a mixed gas comprising oxygen and nitrogen after washing the activated spherical phenol resin with dilute hydrochloric acid, and
a step of sorting the spherical phenol resin after said heat treatment.
5. The process for production of a medical adsorbent according to claim 4 , wherein said spherical phenol resin is obtained using a phenol as the starting material.
6. The process for production of a medical adsorbent according to claim 4 , wherein said spherical phenol resin is obtained using phenols including phenol and at least one methyl group bonded to a phenol nucleus as the starting materials.