Dielectric ceramic composition, electronic device and the production method

1. A production method of a dielectric ceramic composition comprising

a main component including barium titanate expressed by a composition formula of Ba m TiO 2+m , wherein “m” satisfies 0.990<m<1.010,

a fourth subcomponent including an oxide of R, wherein R is at least one selected from the group consisting of Y, La, Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb and Lu, and

other subcomponent including at least BaO;

comprising steps of:

preparing a post-reaction material by bringing a material of said main component to react with a part of a material of said fourth subcomponent to be included in said dielectric ceramic composition in advance of a step of firing;

obtaining a material of said dielectric ceramic composition by adding rest of the material of said fourth subcomponent to be included in said dielectric ceramic composition into said post-reaction material; and

firing said material of said dielectric ceramic composition,

wherein an amount of BaO included in said other subcomponent is n mole with respect to 100 moles of said main component and said main component and said BaO are expressed by a composition formula of Ba m+n/100 TiO 2+m+n/100 , wherein “m” and “n” satisfy 0.994<m+n/100<1.014, and

wherein in said step for preparing the post-reaction material, a content of said fourth subcomponent to be brought to react with the material of said main component is 0.01 mole to 0.2 mole with respect to 100 moles of said main component in terms of R.

2. The production method of a dielectric ceramic composition as set forth in claim 1 , wherein said post-reaction material is obtained by solid state reaction between the material of said main component and the part of the material of said fourth subcomponent.

3. The production method of a dielectric ceramic composition as set forth in claim 1 , wherein a content of said fourth subcomponent in said dielectric ceramic composition to be obtained finally is 0.1 to 10 moles with respect to 100 moles of said main component in terms of R.

4. The production method of a dielectric ceramic composition as set forth in claim 1 , wherein in said step for preparing the post-reaction material, a ratio of said fourth subcomponent to be brought to react with the material of said main component is larger than 0 mol % and smaller than 50 mol % with respect to 100 mol % of a total amount of said fourth subcomponent to be finally included in said dielectric ceramic composition in terms of R.

5. The production method of a dielectric ceramic composition as set forth in claim 1 , wherein

said other subcomponent includes a first subcomponent, a second subcomponent and a third subcomponent,

said first subcomponent includes at least one selected from the group consisting of MgO, GaO, BaO and SrO,

said second subcomponent includes SiO 2 mainly and at least one selected from the group consisting of MO, Li 2 O and B 2 O 3 , wherein M is at least one selected from the group consisting of Mg, Ca, Ba and Sr, and

a third subcomponent includes at least one selected from the group consisting of V 2 O 5 , MoO 3 and WO 3 ; and

ratios of the respective subcomponents with respect to 100 moles of said main component are

the first subcomponent: 0.1 to 5 moles,

the second subcomponent: 0.1 to 12 moles, and

the third subcomponent: more than 0 to 0.3 mole.

6. The production method of a dielectric ceramic composition as set forth in claim 5 , wherein

said other subcomponent furthermore includes a fifth subcomponent including at least one selected from the group consisting of MnO and Cr 2 O 3 , and

a ratio of the fifth subcomponent with respect to 100 moles of said main component is 0.05 to 1.0 mole.

7. The production method of a dielectric ceramic composition as set forth in claim 1 , wherein a material having an average particle diameter of 0.05 to 0.5 μm is used as the material of said main component.