Magnetic disk glass substrate manufacturing method
A magnetic disk glass substrate manufacturing method includes a step of polishing a surface of a glass substrate to a mirror surface, a gas heating process step of causing a heated atmosphere and the glass substrate to contact each other so as to heat the glass substrate at a temperature T 0 , a step of causing a chemically strengthening salt melted exceeding a freezing temperature T F and the glass substrate to contact each other so as to chemically strengthen the glass substrate at a temperature T 1 , a gas cooling process step of causing a gas coolant and the glass substrate to contact each other so as to cool the glass substrate to a temperature T 2 , and a liquid cooling process step of causing a liquid coolant and the glass substrate to contact each other so as to cool the glass substrate to a temperature T 3 , the above-mentioned steps being included in this order, wherein the temperature T 2 is set to a temperature less than the freezing temperature T F of the chemical strengthening salt in a gas cooling process.
1. A magnetic disk glass substrate manufacturing method comprising:
a step of polishing a surface of a glass substrate to a mirror surface;
a step of chemically strengthening the glass substrate by causing a chemical strengthening salt and the glass substrate to contact each other in a heated atmosphere so as to chemically strengthen the glass substrate at a temperature T 1 ;
a gas cooling process step of causing a gas coolant and the glass substrate to contact each other so as to cool the glass substrate to a temperature T 2 ;
a liquid cooling process step of causing a liquid coolant and the glass substrate to contact each other so as to cool the glass substrate to a temperature T 3 ;
the steps being included in this order,
wherein in said gas cooling process step, the glass substrate is cooled from the temperature T 1 to a freezing temperature T F of the chemical strengthening salt within 10 minutes and a cooling speed from the temperature T 1 to the freezing temperature T F is set to 18° C. or more per minute,
wherein in said gas cooling process step, the temperature T 2 is set to a temperature less than a boiling temperature T B of the liquid coolant used in the liquid cooling process,
wherein in said gas cooling process step, the temperature T 2 is set to a temperature less than the freezing temperature T F of the chemical strengthening salt, and
wherein in said gas cooling process step, the glass substrate is cooled from the freezing temperature T F to the temperature T 2 .
2. A magnetic disk glass substrate manufacturing method according to claim 1 , further comprising:
a gas heating process step of subjecting the glass substrate to a heated atmosphere so as to heat the glass substrate at a temperature T 0 ;
wherein in the gas heating process step, the temperature T 0 for heating the glass substrate is set to a temperature higher than the freezing temperature T F of the chemically strengthening salt and lower than a temperature T d of a deformation point of the glass substrate.
3. A magnetic disk glass substrate manufacturing method according to claim 1 , wherein:
in the chemically strengthening step, the temperature T 1 for chemically strengthening the glass substrate is set to a temperature higher than the freezing temperature TF of the chemically strengthening salt and lower than a temperature Td of a deformation point of the glass substrate.
4. A magnetic disk glass substrate manufacturing method according to claim 1 , wherein:
the chemically strengthening salt used in the chemically strengthening step is in a molten state and contains at least one selected from the group consisting of potassium ion, sodium ion, and lithium ion and the liquid coolant used in the liquid cooling process step is water.
5. A method of manufacturing a magnetic disk having at least a magnetic layer formed on the glass substrate manufactured by the manufacturing method according to claim 1 .
6. A magnetic disk glass substrate manufacturing method comprising in order:
a step of polishing a surface of a glass substrate to a mirror surface;
a step of chemically strengthening the glass substrate by causing a chemical strengthening salt and the glass substrate to contact each other in a heated atmosphere so as to chemically strengthen the glass substrate at a temperature T 1 ;
a gas cooling process step of causing a gas coolant and the glass substrate to contact each other so as to cool the glass substrate to a temperature T 2 ;
a liquid cooling process step of causing a liquid coolant and the glass substrate to contact each other so as to cool the glass substrate to a temperature T 3 ;
wherein in said gas cooling process step, the glass substrate is cooled from the temperature T 1 to a freezing temperature T F of the chemical strengthening salt within 10 minutes and a cooling speed from the temperature T 1 to the freezing temperature T F is set to 18° C. or more per minute,
wherein in said gas cooling process step, the temperature T 2 is set to a temperature less than a boiling temperature T B of the liquid coolant used in the liquid cooling process,
wherein in said gas cooling process step, the temperature T 2 is set to a temperature less than the freezing temperature T F of the chemical strengthening salt,
wherein in said gas cooling process step, the glass substrate is cooled from the freezing temperature T F to the temperature T 2 , and
wherein in said gas cooling process step, the glass substrate is cooled from the freezing temperature T F to the temperature T 2 within 10 minutes to 11 minutes.