Method for treating molten metal
The invention relates to a method for treating molten metal that is contained in a metallurgical vessel, according to which a fine-grained blanket material containing silicon oxide and aluminium oxide is spread over the surface of the molten metal. The aim of the invention is to prevent the formation of dust and to facilitate the distribution of the blanket material over the surface of the molten metal. To achieve this, the blanket material consists of a synthetic zeolite material, which contains essentially equal fractions of silicon oxide and aluminium oxide. Said blanket material comprises a close grain-size distribution, in such a way that less than 20% of the grains have a diameter of less than 30 μm or greater than 125 μm. According to an additional embodiment of the invention, a vegetable ash, in particular a rice chaff ash, can be added to the blanket material.
1. A method for treating molten metal contained in a metallurgical vessel, according to which a fine-grained blanket material containing silicon oxide and aluminium oxide is spread over the surface of the molten metal, wherein the blanket material is a synthetic zeolite material which contains essentially equal fractions of silicon oxide and aluminium oxide and which has a close grain-size distribution with less than 20% of the grains measuring less than 30 μm or more than 125 μm in diameter.
2. A method according to claim 1 , wherein the grains of the blanket material are essentially sphere-shaped.
3. A method according to claim 1 wherein the blanket material, prior to being spread over the surface of the molten metal, is blended and/or classified to obtain the desired grain-size distribution.
4. A method according to claim 1 , wherein the ratio of aluminium oxide to silicon oxide contained in the blanket material is larger than or equal to one.
5. A method according to claim 1 , wherein the blanket material contains up to 1% each of titanium oxide, iron oxide, magnesium oxide and calcium oxide.
6. A method according to claim 1 , wherein the molten metal is contained in a steel distributor or a steel casting ladle.
7. A method according to claim 1 , wherein the blanket powder is applied to an intermediate layer of reactive calcium aluminate slag, which is in direct contact with the molten metal.
8. A method according to claim 1 , wherein a carbon source material, e.g. petroleum coke, is added to the blanket material.
9. A method according to claim 1 , wherein the blanket material is applied to the surface of the molten metal in plastic polymer bag portion packs.
10. A method according to claim 1 , wherein vegetable ash is added to the blanket material.
11. The method according to claim 10 , wherein the blanket material is a blend of at least 60% w/w of synthetic zeolite material and up to 40% w/w of vegetable ash.
12. A method according to claim 10 , wherein the blanket material has a vegetable ash content of up to 40% w/w, preferably 20% w/w.
13. The method according to claim 10 , wherein the vegetable ash is rice chaff ash.