Multilayer ceramic capacitor and production method of the same

1. A multilayer ceramic capacitor comprising a capacitor body composed by alternately layering dielectric layers and inner electrode layers,

wherein each of said dielectric layers comprises the following conditions (a) and (b):

(a) comprising a plurality of crystal particles, and grain boundary phases comprising interfacial grain boundaries and triple point grain boundaries formed among a plurality of the crystal particles adjacent to one another; and

(b) Si—Ba—O compound being formed in 5% or more of the triple point grain boundaries in the entire triple point grain boundaries per unit surface area of the dielectric layer.

2. The multilayer ceramic capacitor according to claim 1 , wherein in unit surface area of the dielectric layer, the ratio (C 2 /C 1 ) of a Si concentration C 1 in the interfacial grain boundaries and a Si concentration C 2 in the triple point grain boundaries is 2 or higher.

3. The multilayer ceramic capacitor according to claim 1 , wherein the crystal particles are barium titanate crystal particles with different Ca component concentrations, and the barium titanate crystal particles satisfy the relation A/B≧1.003 by mole ratio in the case barium or barium and Ca is defined as A site, and titanium is defined as B site.

4. The multilayer ceramic capacitor according to claim 3 , wherein the barium titanate crystal particles comprises BT crystal particles with Ca component concentration of 0.2% by atom or lower, and BCT crystal particles with a Ca component concentration of 0.4% by atom or higher, and in the case barium or barium and Ca is defined as A site and titanium is defined as B site in the BCT crystal particles, the A/B ratio by mole satisfies A/B≧1.003.

5. The multilayer ceramic capacitor according to claim 1 , wherein the resistance variation ratio in the grain boundary phases in the dielectric layers before and after a treatment of the highly accelerated life test by an AC impedance method is ±0.7%/min. or lower.

6. A method for producing a multilayer ceramic capacitor, comprising the steps of:

forming a green sheet by adding oxides of Mg, rare earth elements, and Mn, glass powder containing 0.1% by mass or less of alumina, barium carbonate powder, and an organic resin into dielectric powder mixing of a perovskite type barium titanate powder (BCT powder) wherein a portion of A site is replace with Ca, and a perovskite barium titanate powder (BT) containing no substituent Ca;

forming a green body of a capacitor body composed by alternately laminating the green sheets and inner electrode patterns; and sintering the green body of the capacitor body;

wherein in the case the amount of barium and Ca is defined as A, and the amount of titanium is defined as B in the BCT powder, the A/B ratio by mole satisfies A/B≧1.003;

wherein 0.7 to 2 parts by mass of glass powder is added to 100 parts by mass of the dielectric powder; and

wherein 0.01 to 1 parts by mass of the barium carbonate powder is added to 100 parts by mass of the dielectric powder.

7. The method for producing the multilayer ceramic capacitor according to claim 6 , wherein the content of alumina contained in the glass is 0.08% by mass or lower.

8. The method for producing the multilayer ceramic capacitor according to claim 6 , wherein the ratio (W BCT /W BT ) is in a range from 0.95 to 1.05 in the case W BCT denotes the BCT powder amount, and W BT denotes the BT powder amount.