Aqueous primer composition, method of surface treating by using the same and laminated structure thereof
An aqueous primer composition of the present invention includes a water-dispersible polyisocyanate (A) and an acrylic resin water dispersion (B), wherein a polystyrene equivalent weight average molecular weight, determined using gel permeation chromatography, of an acrylic resin in the acrylic resin water dispersion (B) is 350,000 or more, and a glass transition temperature, determined by using a differential scanning calorimeter, of the acrylic resin is 15° C. to 130° C., and a weight ratio between the water-dispersible polyisocyanate (A) and the acrylic resin water dispersion (B) is (A):(B)=70:30 to 50:50.
1. An aqueous primer composition, comprising:
a water-dispersible polyisocyanate (A); and
an acrylic resin water dispersion (B),
wherein a polystyrene equivalent weight average molecular weight, determined using gel permeation chromatography, of an acrylic resin in the acrylic resin water dispersion (B) is 350,000 or more,
a glass transition temperature, determined by using a differential scanning calorimeter, of the acrylic resin is 15° C. to 130° C., and
a weight ratio between the water-dispersible polyisocyanate (A) and the acrylic resin water dispersion (B) is (A):(B)=70:30 to 50:50 in solid content.
2. The aqueous primer composition according to claim 1 , wherein a hydroxyl value of the acrylic resin in the acrylic resin water dispersion (B) is 0 to 60.
3. The aqueous primer composition according to claim 1 , wherein the water-dispersible polyisocyanate (A) is a mixture of a hydrophobic polyisocyanate (A1) and a hydrophilic polyisocyanate (A2), and a weight mixing ratio between the hydrophobic polyisocyanate (A1) and the hydrophilic polyisocyanate (A2) is (A1):(A2)=9:1 to 5:5.
4. The aqueous primer composition according to claim 3 , wherein the hydrophilic polyisocyanate (A2) is a vinyl polymer having an isocyanate group and a hydrophilic group.
5. The aqueous primer composition according to claim 4 , wherein the vinyl polymer is an acrylic polymer having a weight average molecular weight of 2,000 to 100,000.
6. The aqueous primer composition according to claim 4 , wherein the hydrophilic group of the vinyl polymer is a nonionic group.
7. A method of surface-treating an inorganic substrate, comprising: coating
an inorganic substrate used in civil engineering and construction with the aqueous primer composition according to claim 1 .
8. A laminated structure, comprising:
a layer of an inorganic substrate used in civil engineering and construction;
a resin layer formed on the layer of the inorganic substrate with the aqueous primer composition according to claim 1 ; and
a covering resin layer formed on the resin layer with any one of an epoxy resin, a urethane resin, and a polymerizable unsaturated resin.