Titanium alloy and automotive exhaust systems thereof
An oxidation resistant, high strength titanium alloy, particularly adapted for use in the manufacture of automotive exhaust system components and other applications requiring oxidation resistance and strength at elevated temperatures. The alloy comprises, in weight percent, iron less than 0.5, or 0.2 to less than 0.5%, oxygen 0.02 to less than 0.15%, silicon 0.15 to 0.6%, and balance titanium. Optional alloying elements are Al, Nb, V, Mo, Sn, Zr, Ni, Cr and Ta, with a total content of less than 1.5.
1. An oxidation resistant, high strength titanium alloy consisting essentially of, in weight %, 0.2 to less than 0.5 iron, 0.02 to less than 0.12 oxygen, 0.15 to 0.42 silicon and balance titanium and incidental impurities.
2. The alloy of claim 1 , additionally consisting essentially of at least one element selected from the group consisting of Al, Nb, V, Mo, Sn, Zr, Ni, Cr and Ta, with a total content of less than 1.5.
3. The alloy of claim 2 having a minimum UTS of 7 ksi upon testing at a temperature of 1400 F in combination with resistance to oxidation at 1400 F for 100 hours of less than 1% weight gain.
4. A flat rolled product of an oxidation resistant, high strength titanium alloy consisting essentially of, in weight %, 0.2 to less than 0.5 iron, 0.02 to less than 0.12 oxygen, 0.15 to 0.42 silicon and balance titanium and incidental impurities.
5. The flat rolled product of claim 4 wherein said alloy additionally consists essentially of at least one element selected from the group consisting of Al, Nb, V, Mo, Sn, Zr, Ni, Cr and Ta, with a total content of less than 1.5.
6. The flat rolled product of claim 4 in the form of a plate.
7. The flat rolled product of claim 4 in the form of a sheet.
8. Coil strip products, produced by combinations of hot strip rolling, cold strip rolling and annealing, of an oxidation resistant, high strength titanium alloy consisting essentially of, in weight %, 0.2 to less than 0.5 iron, 0.02 to less than 0.12 oxygen, 0.15 to 0.42 silicon and balance titanium and incidental impurities, said alloy having a minimum UTS of 7 ksi upon testing at a temperature of 1400 F in combination with resistance to oxidation at 1400 F for 100 hours of less than 1% weight gain.
9. The coiled product of claim 8 wherein said alloy additionally consists essentially of at least one element selected from the group consisting of Al, Nb, V, Mo, Sn, Zr, Ni, Cr and Ta, with a total content of less than 1.5.
10. An automotive exhaust system component comprising an oxidation resistant, high strength titanium alloy consisting essentially of, in weight %, 0.2 to less than 0.5 iron, 0.02 to less than 0.12 oxygen, 0.15 to 0.42 silicon and balance titanium and incidental impurities.
11. An automotive exhaust system component of claim 10 wherein said alloy additionally consists essentially of at least one element selected from the group consisting of Al, Nb, V, Mo, Sn, Zr, Ni, Cr and Ta, with a total content of less than 1.5.
12. An automotive exhaust system component of claim 11 wherein said alloy has a minimum UTS of 7 ksi upon testing at a temperature of 1400 F in combination with resistance to oxidation at 1400 F for 100 hours of less than 1% weight gain.
13. A muffler comprising an oxidation resistant, high strength titanium alloy consisting essentially of, in weight %, 0.2 to less than 0.5 iron, 0.02 to less than 0.12 oxygen, 0.15 to 0.42 silicon and balance titanium and incidental impurities.
14. A muffler comprising an oxidation resistant, high strength titanium alloy of claim 13 wherein said alloy additionally consists essentially of at least one element selected from the group consisting of Al, Nb, V, Mo, Sn, Zr, Ni, Cr and Ta, with a total content of less than 1.5.
15. A muffler comprising an oxidation resistant, high strength titanium alloy of claim 14 wherein said alloy has a minimum UTS of 7 ksi upon testing at a temperature of 1400 F in combination with resistance to oxidation at 1400 F for 100 hours of less than 1% weight gain.
16. A flat rolled product comprising a plate of a titanium alloy consisting essentially of, in weight %, 0.2 to less than 0.5 iron, 0.02 to less than 0.12 oxygen, 0.15 to 0.42 silicon and balance titanium and incidental impurities.
17. The flat rolled product of claim 16 wherein said titanium alloy additionally consists essentially of at least one element selected from the group consisting of Al, Nb, V, Mo, Sn, Zr, Ni, Cr and Ta, with a total content of less than 1.5.
18. The flat rolled product of claim 16 wherein said titanium alloy has a minimum UTS of 7 ksi upon testing at a temperature of 1400° F. in combination with a resistance to oxidation at 1400° F. for 100 hours of less than 1% weight gain.
19. A flat rolled product comprising a sheet of a titanium alloy consisting essentially of, in weight %, 0.2 to less than 0.5 iron, 0.02 to less than 0.12 oxygen, 0.15 to 0.42 silicon and balance titanium and incidental impurities.
20. The flat rolled product of claim 19 wherein said titanium alloy additionally consists essentially of at least one element selected from the group consisting of Al, Nb, V, Mo, Sn, Zr, Ni, Cr and Ta, with a total content of less than 1.5.
21. The flat rolled product of claim 19 wherein said titanium alloy has a minimum UTS of 7 ksi upon testing at a temperature of 1400° F. in combination with a resistance to oxidation at 1400° F. for 100 hours of less than 1% weight gain.
22. A flat rolled product comprising a coil strip of a titanium alloy consisting essentially of, in weight %, 0.2 to less than 0.5 iron, 0.02 to less than 0.12 oxygen, 0.15 to 0.42 silicon and balance titanium and incidental impurities.
23. The flat rolled product of claim 22 wherein said titanium alloy additionally consists essentially of at least one element selected from the group consisting of Al, Nb, V, Mo, Sn, Zr, Ni, Cr and Ta, with a total content of less than 1.5.
24. The flat rolled product of claim 22 wherein said titanium alloy has a minimum UTS of 7 ksi upon testing at a temperature of 1400° F. in combination with a resistance to oxidation at 1400° F. for 100 hours of less than 1% weight gain.
25. An elevated-temperature oxidation resistant, high strength titanium alloy consisting essentially of, in weight %, 0.2 to less than 0.5 iron, 0.02 to less than 0.12 oxygen, 0.15 to 0.42 silicon and balance titanium and incidental impurities.
26. The alloy of claim 25 wherein said titanium alloy additionally consists essentially of at least one element selected from the group consisting of Al, Nb, V, Mo, Sn, Zr, Ni, Cr and Ta, with a total content of less than 1.5.
27. The alloy of claim 25 wherein said alloy has a minimum UTS of 7 ksi upon testing at a temperature of 1400° F. in combination with a resistance to oxidation at 1400° F. for 100 hours of less than 1% weight gain.
28. An alloy having a minimum UTS of 9 ksi upon testing at a temperature of 1400 F in combination with resistance to oxidation at 1400 F for 100 hours of less than 0.8% weight gain consisting essentially of, in weight %, 0.2 to less than 0.5 iron, 0.02 to less than 0.12 oxygen, 0.15 to 0.42 silicon and balance titanium and incidental impurities.
29. A titanium alloy consisting essentially of, in weight %, 0.49 iron, 0.10 oxygen, 0.42 silicon and balance titanium and incidental impurities, said alloy having a minimum UTS of 9 ksi upon testing at a temperature of 1400 F in combination with resistance to oxidation at 1400 F for 100 hours of less than 0.8% weight gain.
30. An automotive exhaust system component comprising a titanium alloy consisting essentially of, in weight % 0.2 to less than 0.5 iron, 0.02 to less than 0.12 oxygen, 0.15 to 0.42 silicon and balance titanium and incidental impurities, said alloy having a minimum UTS of 7 ksi upon testing at a temperature of 1400 F in combination with resistance to oxidation at 1400 F for 100 hours of less than 1% weight gain.