Method for production of moulded bodies, in particular optical structures and use thereof
View Patent ↗The present invention relates to a method for manufacture a body from a thermoplastic plastic with a three-dimensionally structured surface, wherein molding is performed directly from a master made of glass coated with metal oxide, without deposition of further coatings on a surface of the master. The invention also relates to bodies manufactured with this method from a thermoplastic featuring a three-dimensionally structured surface, as well as to planar optical structures likewise manufactured with this method for generating evanescent-field measuring platforms and to a use thereof. The invention furthermore relates to a planar optical structure for generating an evanescent-field measuring platform, comprising a first essentially optical transparent, waveguiding layer (a) with refractive index n 1 and a second essentially optical transparent layer (b) with refractive index n 2 , where n 1 >n 2 , in a case of an embodiment of a planar optical film waveguide, or comprising a metal layer (a′) and a second layer (b), in a case of an embodiment for generating a surface plasmon resonance, wherein the second layer (b) comprises a material from a group comprising cyclo-olefin polymers and cyclo-olefin copolymers.
1. A method for manufacturing an evanescent-field measuring platform including a first layer and a second layer, said second layer being made of an essentially optically transparent thermoplastic plastic comprising manufacturing of said second layer using a master,
wherein said master is a glass master having a surface coated with metal oxide,
wherein said manufacturing of said second layer includes directly molding said thermoplastic plastic using said master as part of a molding tool, without deposition of further coatings on said coated surface of said master prior to said directly molding.
2. The method according to claim 1 , wherein
said manufacturing an evanescent-field measuring platform further comprises manufacturing a metal layer, as said first layer on said second layer.
3. The method according to claim 2 , wherein
raised areas are on the surface of said master such that using said master to produce said second layer results in recesses existing in a surface of said second layer.
4. The method according to claim 3 , wherein
said recesses have a depth of from 20 μm to 500 μm.
5. The method according to claim 3 , wherein
said recesses have a depth of from 50 μm to 300 μm.
6. The method according to claim 2 , wherein
a grating structure and raised areas are on the surface of said master such that using said master to produce said second layer results in a grating and recesses simultaneously existing in a surface of said second layer.
7. The method according to claim 6 , wherein
said grating has a depth of from 3 nm to 100 nm, and
said recesses have a depth of from 20 μm to 500 μm.
8. The method according to claim 6 , wherein
said grating has a depth of from 10 nm to 30 nm, and
said recesses have a depth of from 50 μm to 300 μm.
9. The method according to claim 2 , wherein
said manufacturing an evanescent-field measuring platform comprises manufacturing a planar optical structure for generating a surface plasmon resonance.
10. The method according to claim 2 , wherein
said metal oxide comprises a material selected from the group consisting of TiO 2 , ZnO, Nb 2 O 5 , Ta 2 O 5 , HfO 2 and ZrO 2 .
11. The method according to claim 2 , wherein
a grating structure is on the surface of said master such that using said master to produce said second layer results in a grating existing in a surface of said second layer.
12. The method according to claim 2 , wherein
said directly molding comprises one of
(i) directly molding said thermoplastic plastic using said master during an injection molding process,
(ii) directly molding said thermoplastic plastic using said master during a reaction injection molding process,
(iii) directly molding said thermoplastic plastic using said master during a liquid injection molding process, and
(iv) directly molding said thermoplastic plastic using said master during a hot embossing process.
13. The method according to claim 2 , wherein
said directly molding comprises directly molding said thermoplastic plastic using said master during an injection molding process.
14. The method according to claim 2 , wherein
said directly molding comprises directly molding said thermoplastic plastic using said master during a variotherm injection molding process.
15. The method according to claim 2 , wherein
said directly molding comprises directly molding a material selected from the group consisting of polycarbonates, polymethylmethacrylates, cyclo-olefin polymers and cyclo-olefin copolymers.
16. The method according to claim 2 , wherein
said directly molding comprises directly mold directly molding a material selected from the group consisting of cyclo-olefin polymers and cyclo-olefin copolymers.
17. The method according to claim 1 , wherein
said manufacturing an evanescent-field measuring platform including a first layer and a second layer, produced by using said master, further comprises manufacturing an essentially optically transparent waveguiding layer having a refractive index n 1 , as said first layer, on an essentially optically transparent thermoplastic plastic layer having a refractive index n 2 , as said second layer, with n 1 >n 2 .
18. The method according to claim 17 , wherein
raised areas are on the surface of said master such that using said master to produce said second layer results in recesses existing in a surface of said second layer.
19. The method according to claim 18 , wherein
said recesses have a depth of from 20 μm to 500 μm.
20. The method according to claim 18 , wherein
said recesses have a depth of from 50 μm to 300 μm.
21. The method according to claim 17 , wherein
a grating structure and raised areas are on the surface of said master such that using said master to produce said second layer results in a grating and recesses simultaneously existing in a surface of said second layer.
22. The method according to claim 21 , wherein
said grating has a depth of from 3 nm to 100 nm, and
said recesses have a depth of from 20 μm to 500 μm.
23. The method according to claim 21 , wherein
said grating has a depth of from 10 nm to 30 nm, and
said recesses have a depth of from 50 μm to 300 μm.
24. The method according to claim 17 , wherein
said manufacturing an evanescent-field measuring platform comprises manufacturing a planar optical structure for generating a surface plasmon resonance.
25. The method according to claim 17 , wherein
said manufacturing an evanescent-field measuring platform comprises manufacturing a planar optical film waveguide.
26. The method according to claim 17 , wherein
said metal oxide comprises a material selected from the group consisting of TiO 2 , ZnO, Nb 2 O 5 , Ta 2 O 5 , HfO 2 and ZrO 2 .
27. The method according to claim 17 , wherein
a grating structure is on the surface of said master such that using said master to produce said second layer results in a grating existing in a surface of said second layer.
28. The method according to claim 17 , wherein
said directly molding comprises one of
(i) directly molding said thermoplastic plastic using said master during an injection molding process,
(ii) directly molding said thermoplastic plastic using said master during a reaction injection molding process,
(iii) directly molding said thermoplastic plastic using said master during a liquid injection molding process, and
(iv) directly molding said thermoplastic plastic using said master during a hot embossing process.
29. The method according to claim 17 , wherein
said directly molding comprises directly molding said thermoplastic plastic using said master during an injection molding process.
30. The method according to claim 17 , wherein
said directly molding comprises directly molding said thermoplastic plastic using said master during a variotherm injection molding process.
31. The method according to claim 17 , wherein
said directly molding comprises directly molding a material selected from the group consisting of polycarbonates, polymethylmethacrylates, cyclo-olefin polymers and cyclo-olefin copolymers.
32. The method according to claim 17 , wherein
said directly molding comprises directly molding a material selected from the group consisting of cyclo-olefin polymers and cyclo-olefin copolymers.
33. The method according to claim 1 , wherein
raised areas are on the surface of said master such that using said master to produce said second layer results in recesses existing in a surface of said second layer.
34. The method according to claim 33 , wherein
said recesses have a depth of from 20 μm to 500 μm.
35. The method according to claim 33 , wherein
said recesses have a depth of from 50 μm to 300 μm.
36. The method according to claim 1 , wherein
a grating structure and raised areas are on the surface of said master such that using said master to produce said second layer results in a grating and recesses simultaneously existing in a surface of said second layer.
37. The method according to claim 36 , wherein
said grating has a depth of from 3 nm to 100 nm, and
said recesses have a depth of from 20 μm to 500 μm.
38. The method according to claim 36 , wherein
said grating has a depth of from 10 nm to 30 nm, and
said recesses have a depth of from 50 μm to 300 μm.
39. The method according to claim 1 , wherein
said manufacturing an evanescent-field measuring platform comprises manufacturing a planar optical structure for generating a surface plasmon resonance.
40. The method according to claim 1 , wherein
said metal oxide comprises a material selected from the group consisting of TiO 2 , ZnO, Nb 2 O 5 , Ta 2 O 5 , HfO 2 and ZrO 2 .
41. The method according to claim 1 , wherein
a grating structure is on the surface of said master such that using said master to produce said second layer results in a grating existing in a surface of said second layer.
42. The method according to claim 1 , wherein
said directly molding comprises one of
(i) directly molding said thermoplastic plastic using said master during an injection molding process,
(ii) directly molding said thermoplastic plastic using said master during a reaction injection molding process,
(iii) directly molding said thermoplastic plastic using said master during a liquid injection molding process, and
(iv) directly molding said thermoplastic plastic using said master during a hot embossing process.
43. The method according to claim 1 , wherein
said directly molding comprises directly molding said thermoplastic plastic using said master during an injection molding process.
44. The method according to claim 1 , wherein
said directly molding comprises directly molding said thermoplastic plastic using said master during a variotherm injection molding process.
45. The method according to claim 1 , wherein
said directly molding comprises directly molding a material selected from the group consisting of polycarbonates, polymethylmethacrylates, cyclo-olefin polymers and cyclo-olefin copolymers.
46. The method according to claim 1 , wherein
said directly molding comprises directly molding a material selected from the group consisting of cyclo-olefin polymers and cyclo-olefin copolymers.
47. The method according to claim 2 , wherein
said metal oxide comprises a material selected from the group consisting of TiO 2 , Nb 2 O 5 and Ta 2 O 5 .
48. The method according to claim 17 , wherein
said metal oxide comprises a material selected from the group consisting of TiO 2 , Nb 2 O 5 and Ta 2 O 5 .
49. The method according to claim 1 , wherein
said metal oxide comprises a material selected from the group consisting of TiO 2 , Nb 2 O 5 and Ta 2 O 5 .