pH-controlled photosynthesis of silver nanoprisms

1. A process for the production of monodisperse triangular Type II silver nanoprisms comprising:

irradiating a mixture comprising silver nanocrystals with light having a first narrow band of wavelengths to form triangular Type I silver nanoprisms having unimodal size distribution, the mixture having a pH of about 10 to about 12; and

irradiating a solution comprising the triangular Type I silver nanoprisms with light having a second narrow band of wavelengths to form triangular Type II silver nanoprisms having a unimodal size distribution and at least one edge length of about 100 nm to about 500 nm, the solution having a pH of about 6 to up to 8.

2. The process of claim 1 , wherein the silver nanocrystals are formed in situ by admixing a silver salt and a reducing agent under conditions sufficient to form the silver nanocrystals.

3. The process of claim 2 , wherein the silver salt is selected from the group consisting of silver nitrate, silver acetate, silver perchlorate, silver sulfate, and mixtures thereof.

4. The process of claim 2 , wherein the reducing agent is selected from the group consisting of sodium borohydride, sodium triacetoxy borohydride, diisobutylaluminum hydride, potassium tri-sec-butylborohydride, potassium triethylborohydride, sodium tri-sec-butylborohydride, lithium triethylborohydride, lithium tri-sec-butylborohydride, methyl oxazaborolidine, diisopinocampheylchloroborane, methoxydiethylborane, dibutylboron triflate, dicyclohexylboron triflate, dicyclohexylchloroborane, borane-tetrahydrofuran complex, dimethylsulfide borane, diethylaniline borane, tert-butylamine borane, morpholine borane, dimethylamine borane, triethylamine borane, pyridine borane, and mixtures thereof.

5. The process of claim 2 , wherein the silver salt comprises silver nitrate and the reducing agent comprises sodium borohydride.

6. The process of claim 2 , wherein the admixture to form silver nanocrystals in situ further comprises at least one separation agent.

7. The process of claim 6 , wherein the at least one separation agent comprises bis(p-sulfonatophenyl)phenylphosphine, citric acid or a salt thereof, or mixtures thereof.

8. The process of claim 1 , wherein the first or second narrow band of wavelengths is selected from the group consisting of about 470±5 nm, about 488±5 nm, about 500±5 nm, about 514±5 nm, about 550±20 nm, about 600±20 nm, and about 633±20 nm.

9. The process of claim 1 , wherein the pH of the mixture is about 10 to about 11.5.

10. The process of claim 9 , wherein the pH of the mixture is about 10.5 to about 11.5.

11. The process of claim 1 , wherein at least one edge length of the triangular Type I silver nanoprisms is about 30 nm to about 80 nm.

12. The process of claim 11 , wherein at least one edge length of the Type I silver nanoprisms is about 50 nm to about 70 nm.

13. The process of claim 1 , wherein the at least one edge length of the Type II nanoprisms is about 100 nm to about 200 nm.

14. The process of claim 1 , wherein the pH of the solution of silver nanoprisms is about 6 to about 7.9.

15. The process of claim 14 , wherein the pH of the solution is about 7 to about 7.5.