Oil based blends of interpolymers of ethylene/α-olefins

1. A polymer blend comprising:

(i) at least one ethylene/α-olefin interpolymer, wherein the ethylene/α-olefin interpolymer is a block interpolymer and:

(a) has a Mw/Mn from about 1.7 to about 3.5, at least one melting point, Tm, in degrees Celsius, and a density, d, in grams/cubic centimeter, wherein the numerical values of Tm and d correspond to the relationship:

T m ≧−2002.9+4538.5( d )−2422.2( d ) 2 ; or

(b) has a Mw/Mn from about 1.7 to about 3.5, and is characterized by a heat of fusion, ΔT in J/g, and a delta quantity, ΔT, in degrees Celsius defined as the temperature difference between the tallest DSC peak and the tallest CRYSTAF peak, wherein the numerical values of ΔT and ΔH have the following relationships:

Δ T >−0.1299(ΔH)+62.81 for Δ H greater than zero and up to 130 J/g,

Δ T ≧48° C. for Δ H greater than 130 J/g,

wherein the CRYSTAF peak is determined using at least 5 percent of the cumulative polymer, and if less than 5 percent of the polymer has an identifiable CRYSTAF peak, then the CRYSTAF temperature is 30° C.; or

(c) is characterized by an elastic recovery, Re, in percent at 300 percent strain and 1 cycle measured with a compression-molded film of the ethylene/α-olefin interpolymer, and has a density, d, in grams/cubic centimeter, wherein the numerical values of Re and d satisfy the following relationship when the ethylene/α-olefin interpolymer is substantially free of a cross-linked phase:

Re >1481−1629( d ); or

(d) has a molecular fraction which elutes between 40° C. and 130° C. when fractionated using TREF, characterized in that the fraction has a molar comonomer content of at least 5 percent higher than that of a comparable random ethylene interpolymer fraction eluting between the same temperatures, wherein said comparable random ethylene interpolymer has the same comonomer(s) and has a melt index, density, and molar comonomer content (based on the whole polymer) within 10 percent of that of the ethylene/α-olefin interpolymer; or

(e) is characterized by a storage modulus at 25° C., G′(25° C.), and a storage modulus at 100° C., G′(100° C.), wherein the ratio of G′(25° C.) to G′(100° C.) is from about 1:1 to about 10:1; and

(ii) at least one oil.

2. The polymer blend of claim 1 , wherein the ethylene/α-olefin interpolymer has a Mw/Mn from about 1.7 to about 3.5, at least one melting point, Tm, in degrees Celsius, and a density, d, in grams/cubic centimeter, wherein the numerical values of Tm and d correspond to the relationship:

T m ≧858.91−1825.3( d )+1112.8( d ) 2 .

3. The polymer blend of claim 1 , wherein the ethylene/α-olefin interpolymer has a Mw/Mn from about 1.7 to about 3.5 and is characterized by a heat of fusion, ΔH in J/g, and a delta quantity, ΔT, in degrees Celsius defined as the temperature difference between the tallest DSC peak and the tallest CRYSTAF peak, wherein the numerical values of ΔT and ΔH have the following relationships:

Δ T >−0.1299(Δ H )+62.81 for Δ H greater than zero and up to 130 J/g,

Δ T ≧48° C. for Δ H greater than 130 J/g,

wherein the CRYSTAF peak is determined using at least 5 percent of the cumulative polymer, and if less than 5 percent of the polymer has an identifiable CRYSTAF peak, then the CRYSTAF temperature is 30° C.

4. The polymer blend of claim 1 , wherein the ethylene/α-olefin interpolymer is characterized by an elastic recovery, Re, in percent at 300 percent strain and 1 cycle measured with a compression-molded film of the ethylene/α-olefin interpolymer, and has a density, d, in grams/cubic centimeter, wherein the numerical values of Re and d satisfy the following relationship when the ethylene/α-olefin interpolymer is substantially free of a cross-linked phase:

Re >1481−1629( d ).

5. The polymer blend of claim 4 , wherein the numerical values of Re and d satisfy the following relationship:

Re >1491−1629( d ).

6. The polymer blend of claim 4 , wherein the numerical values of Re and d satisfy the following relationship:

Re >1501−1629( d ).

7. The polymer blend of claim 4 , wherein the numerical values of Re and d satisfy the following relationship:

Re >1511−1629( d ).

8. The polymer blend of claim 1 , wherein the ethylene/α-olefin interpolymer has a molecular fraction which elutes between 40° C. and 130° C. when fractionated using TREF, characterized in that the fraction has a molar comonomer content of at least 5 percent higher than that of a comparable random ethylene interpolymer fraction eluting between the same temperatures, wherein said comparable random ethylene interpolymer has the same comonomer(s) and has a melt index, density, and molar comonomer content (based on the whole polymer) within 10 percent of that of the ethylene/α-olefin interpolymer.

9. The polymer blend of claim 1 , wherein the ethylehe/α-olefin interpolymer is characterized by a storage modulus at 25° C., G′(25° C.), and a storage modulus at 100° C., G′(100° C.), wherein the ratio of G′(25° C.) to G′(100° C.) is from about 1:1 to about 10:1.

10. The polymer blend of claim 1 , wherein the α-olefin in the ethylene/α-olefin interpolymer is styrene, propylene, 1-butene, 1-hexene, 1-octene, 4-methyl-1-pentene, norbornene, 1-decene, 1,5-hexadiene, or a combination thereof.

11. The polymer blend of claim 1 , wherein the ethylene/α-olefin interpolymer is present in the range from about 50% to about 95% by weight of the total composition.

12. The polymer blend of claim 1 , wherein the oil is an aromatic oil, napththenic oil, paraffinic oil or a combination thereof.

13. The polymer blend of claim 1 , wherein the blend comprises oil in an amount up to and including about 50 wt %.

14. The polymer blend of claim 1 , wherein the blend comprises oil in an amount from about 5 wt % to about 50 wt %.

15. The polymer blend of claim 1 , wherein the blend comprises oil in an amount from about 10 wt % to about 40 wt %.

16. The polymer blend of claim 1 , wherein the blend comprises oil in amount from about 20 wt % to about 30 wt %.

17. The polymer blend of claim 1 , wherein the blend comprises oil in amount from about 10 wt % to about 20 wt %.

18. The polymer blend of claim 1 , wherein the blend comprises oil in an amount from about 10 wt % to about 50 wt %.

19. The polymer blend of claim 1 , further comprising at least an additive.

20. The polymer blend of claim 19 , wherein the additive is a slip agent, anti-blocking agent, plasticizer, antioxidant, UV stabilizer, colorant or pigment, filler, lubricant, antifogging agent, flow aid, coupling agent, cross-linking agent, nucleating agent, surfactant, solvent, flame retardant, antistatic agent or a combination thereof.

21. A flexible molded article comprising the polymer blend of claim 1 .

22. The flexible molded article of claim 21 , wherein the flexible molded article is selected from the group consisting of toys, grips, soft touch handles, bumper rub strips, floorings, auto floor mats, wheels, casters, furniture and appliance feet, tags, seals, gaskets, static gaskets, dynamic gaskets, automotive doors, bumper fascia, grill components, rocker panels, hoses, linings, office supplies, seals, liners, diaphragms, tubes, lids, stoppers, plunger tips, delivery systems, kitchen wares, shoes, shoe bladders, shoe soles and combinations thereof.

23. A flexible molded article comprising the polymer blend of claim 19 .

24. The flexible molded article of claim 23 , wherein the flexible molded article is selected from the group consisting of toys, grips, soft touch handles, bumper rub strips, floorings, auto floor mats, wheels, casters, furniture and appliance feet, tags, seals, gaskets, static gaskets, dynamic gaskets, automotive doors, bumper fascia, grill components, rocker panels, hoses, linings, office supplies, seals, liners, diaphragms, tubes, lids, stoppers, plunger tips, delivery systems, kitchen wares, shoes, shoe bladders, shoe soles and combinations thereof.