Ceramic materials for friction linings
Ceramic friction linings comprising a material consisting essentially of metal oxides which are present in the form of a sintered ceramic or in the form of ceramic particles bound by carbon and/or carbides, processes for producing them and their use in combination with ceramic friction bodies, in particular for high-performance brakes.
1. A process for producing a ceramic brake lining comprising a material consisting essentially of magnesium oxide which is present in the form of ceramic particles bound by carbon and/or carbides, wherein the material has a mass fraction of at least 50% of magnesium oxide, wherein the cohesion of the material is effected by bonding with carbides, wherein
a shapeable mixture of pulverulent magnesium oxide, carbide-forming metals selected from the group consisting of Ti, Ni, and Cr, additives comprising carbon fibres be present in a volume fraction up to 35%, and thermally curing organic binders is produced in a first step,
this mixture is brought into the desired shape by pressing in a second step to provide a shaped mixture, and
the shaped mixture is cured to produce a green body with the aid of the said thermally curing organic binders in a third step, and
the green body produced in this way is carbonised in a fourth step at temperatures above 650° C. and in the absence of atmospheric oxygen, wherein carbon is formed during carbonisation, and
carbides are formed in a thermal treatment carried out at a temperature of at least 1200° C. from the added carbide-forming metals selected from the group consisting of Ti, Ni, and Cr, and the carbon formed during the said carbonisation by decomposition of the said organic binders,
which carbides form an inorganic binder phase during the said thermal treatment and bind the said magnesium oxide.
2. The process of claim 1 wherein the additives are selected from the group consisting of inorganic binders, friction promoters and lubricants with the sum of the mass fractions of the additives in the materials being below 50%.
3. The process of claim 2 wherein the friction promoters are selected from the group consisting of aluminum oxide, zirconium dioxide, zircon (ZrSiO4), silicon carbide and silicon dioxide.
4. The process of claim 2 wherein the lubricants are selected from the group consisting of molybdenum disulfide, graphite and boron nitride.
5. The process as claimed in claim 1 , wherein the sum of the mass fractions of carbon and carbides in the material forming the friction lining is in the range from 5% to 50%.
6. The process as claimed in claim 1 , wherein the carbon fibres are in a mass fraction of from 10% to 30%.
7. A process for producing a ceramic brake lining comprising a material consisting essentially of magnesium oxide which is present in the form of ceramic particles bound by carbon and/or carbides, wherein the material has a mass fraction of at least 50% of magnesium oxide, wherein the cohesion of the material is effected by bonding with carbides, wherein
a shapeable mixture of pulverulent magnesium oxide, carbide-forming metals selected from the group consisting of Ti, Ni, and Cr, additives comprising carbon fibres be present in a mass fraction of from 10 to 30%, and thermally curing organic binders is produced in a first step,
this mixture is brought into the desired shape by pressing in a second step to provide a shaped mixture, and
the shaped mixture is cured to produce a green body with the aid of the said thermally curing organic binders in a third step, and
the green body produced in this way is carbonised in a fourth step at temperatures above 650° C. and in the absence of atmospheric oxygen, wherein carbon is formed during carbonisation, and
carbides are formed in a thermal treatment carried out at a temperature of at least 1200° C. from the added carbide-forming metals selected from the group consisting of Ti, Ni, and Cr, and the carbon formed during the said carbonisation by decomposition of the said organic binders, which carbides form an inorganic binder phase during the said thermal treatment and bind the said magnesium oxide.
8. The process of claim 7 wherein the additives are selected from the group consisting of inorganic binders, friction promoters and lubricants with the sum of the mass fractions of the additives in the materials being below 50%.
9. The process of claim 8 , wherein the friction promoters are selected from the group consisting of aluminum oxide, zirconium dioxide, zircon (ZrSiO4), silicon carbide and silicon dioxide.
10. The process of claim 8 , wherein the lubricants are selected from the group consisting of molybdenum disulfide, graphite and boron nitride.
11. The process as claimed in claim 7 , wherein the sum of the mass fractions of carbon and carbides in the material forming the friction lining is in the range from 5% to 50%.