Optical glass
An optical glass includes, in percent by weight, 2-11% SiO 2 , 28-45% B 2 O 3 , 2-15% CaO, 3-18% ZnO, 1-8% ZrO 2 , 9-40% La 2 O 3 , 0.5-11% Gd 2 O 3 , 0-10% Y 2 O 3 , 0-3% Al 2 O 3 , at most 8% R 2 O, where R 2 O is selected from the group consisting of Li 2 O, Na 2 O and K 2 O, at most 20% R′O, where R′O is selected from the group consisting of MgO, CaO, SrO and BaO, 0-3% WO 3 , 0-2% Nb 2 O 5 , and 0-1% Sb 2 O 3 . The optical glass is free from environmental and human harmful components such as PbO and As 2 O 3 . The optical glass has a refractive index in the range of 1.66-1.72, an Abbe number in the range of 51-56, a liquidus temperature (LT) of at most 1000° C. and a raw material melting temperature of at most 1300° C. The optical glass is suitable for mass production, and is stable against devitrification during manufacturing of preforms and precision molding of lenses.
1. An optical glass comprising, in percent by weight, 2-11% SiO 2 , 28-45% B 2 O 3 , 2-12% CaO, 3-18% ZnO, 1-8% ZrO 2 , 9-40% La 2 O 3 , 0.5-11% Gd 2 O 3 , 0-10% Y 2 O 3 , 0-3% Al 2 O 3 , at most 8% R 2 O, where R 20 is the total of Li 2 O, Na 2 O and K 2 O, at most 20% R′O, where R′O is the total of MgO, CaO, SrO and BaO, 1-7% Li 2 O, 6-8% SrO, 0-3% WO 3 , 0-2% Nb 2 O 5 , and 0-1% Sb 2 O 3 .
2. The optical glass as claimed in claim 1 exhibiting a refractive index in the range of 1.66-1.72, and an Abbe number in the range of 51-56.
3. The optical glass as claimed in claim 1 having a glass liquidus temperature equal to or lower than 1000° C., and a raw material melting temperature equal to or lower than 1300° C.
4. An optical glass comprising, in percent by weight, 6-11% SiO 2 , 28-40% B 2 O 3 , 2-12% CaO, 5-18% ZnO, 1-8% ZrO 2 , 9-30% La 2 O 3 , 1-11% Gd 2 O 3 , 1-10% Y 2 O 3 , 1-7% Li 2 O, at most 8% R 2 O, where R 2 O is the total of Li 2 O, Na 2 O and K 2 O, 6-8% SrO, at most 20% R′O where R′O is the total of MgO, CaO, SrO and BaO, 0-3% WO 3 , 0-2% Nb 2 O 5 , and 0-1% Sb 2 O 3 .
5. The optical glass as claimed in claim 4 exhibiting a refractive index in the range of 1.66-1.72, and an Abbe number in the range of 51-56.
6. The optical glass as claimed in claim 4 having a glass liquidus temperature equal to or lower than 1000° C., and a raw material melting temperature equal to or lower than 1300° C.