Polymer membrane for fuel cell, method of preparing same, and membrane-electrode assembly for fuel cell comprising same
The polymer electrolyte membrane of the present invention includes polymers having a fluoroalkyl group and a proton conductive group. The present invention also provides a membrane-electrode assembly, a fuel cell system including the polymer electrolyte membrane, and a method of making the polymer electrolyte membrane by a chemical grafting method. The amount of the proton conductive groups in the polymer electrolyte membrane can be controlled, the membrane thickness can be easily controlled, adherence between a polymer electrolyte membrane and an electrode is improved due to the fluoroalkyl of the polymer, and long-term stability of a membrane-electrode assembly is improved.
1. A polymer electrolyte membrane for a fuel cell, comprising a polymer of Formula 1:
wherein R 1 to R 3 are the same or different, and are fluorine, hydrogen, or a substituted or unsubstituted alkyl group, and at least one of R 1 to R 3 is fluorine or an alkyl group substituted with fluorine;
R 4 to R 6 are independently —O—, —S—, —CO—, —SO 2 —, or —P(Ph)O where Ph is phenyl-;
R 7 to R 10 are independently hydrogen, a substituted or unsubstituted alkyl group, a substituted or unsubstituted heteroalkyl group, a substituted or unsubstituted aryl group, or a substituted or unsubstituted heteroaryl group;
R 11 is —O—, —S—, —CO—, or —SO 2 —;
l and m are independently an integer ranging from 0 to 24;
w is an integer ranging from 1 to 20;
k is an integer ranging from 1 to 1000;
x is an integer ranging from 100 to 100,000;
y is an integer ranging from 1 to 100,000;
z is an integer ranging from 1 to 10,000; and
Y is a proton conductive group.
2. The polymer electrolyte membrane of claim 1 , wherein the Y is selected from the group consisting of sulfonic acid, carboxylic acid, phosphoric acid, and salts thereof.
3. The polymer electrolyte membrane of claim 2 , wherein the salts are selected from the group consisting of Na salts, K salts, Li salts, Ca salts, and combinations thereof.
4. The polymer electrolyte membrane of claim 1 , wherein R 1 to R 3 are all fluorine.
5. The polymer electrolyte membrane of claim 1 , wherein the polymer has a weight average molecular weight ranging from 10,000 to 1,000,000.
6. The polymer electrolyte membrane of claim 1 , wherein the polymer is represented by Formula 1a:
7. A method of preparing a polymer electrolyte membrane comprising:
preparing a polymer of Formula 3:
performing radical polymerization of the compound of Formula 3 to obtain a polymer of Formula 1; and
forming a membrane using the polymer of Formula 1:
wherein R 1 to R 3 are the same or different and are fluorine, hydrogen, or a substituted or unsubstituted alkyl group, and at least one of R 1 to R 3 is fluorine or an alkyl group substituted with fluorine;
R 4 to R 6 are independently —O—, —S—, —CO—, —SO 2 —, or —P(Ph)O—;
R 7 to R 10 are independently hydrogen, a substituted or unsubstituted alkyl group, a substituted or unsubstituted heteroalkyl group, a substituted or unsubstituted aryl group, or a substituted or unsubstituted heteroaryl group;
R 11 is —O—, —S—, —CO—, or —SO 2 —;
l and m are independently an integer ranging from 0 to 24,
w is an integer ranging from 1 to 20,
k is an integer ranging from 1 to 1000,
x is an integer ranging from 100 to 100,000,
y is an integer ranging from 1 to 10,000,
z is an integer ranging from 1 to 10,000,
Y is a proton conductive group,
a is an integer ranging from 500 to 100,000,
b is an integer ranging from 1 to 50,000, and
X is Br, Cl, or I.
8. The method of claim 7 , wherein the preparation of the compound of Formula 3 comprises halogenating a compound of Formula 2:
9. The method of claim 7 , wherein the Y is selected from the group consisting of sulfonic acid, carboxylic acid, phosphoric acid, and salts thereof.
10. The method of claim 9 , wherein the salts are selected from the group consisting of Na salts, K salts, Li salts, Ca salts, and combinations thereof.
11. The method of claim 7 , wherein the mole ratio of a and b in the above Formula 3 is the range of 10:1 to 5:1.
12. The method of claim 7 , wherein the radical polymerization reaction is performed at a temperature of 50 to 150° C. for 4 to 48 hours.
13. The method of claim 7 , wherein the radical polymerization reaction comprises chemical-reacting a halogen-substituted alkoxide with the compound of Formula 3, and then adding an aryl having an ethylene group and a proton conductive group to the resultant compound to obtain a mixture, and performing the radical polymerization.
14. The method of claim 13 , wherein the halogen-substituted alkoxide is perfluoropropoxide or its salt, and the aryl having the ethylene group and the proton conductive group is styrene sulfonic acid or its salt.
15. The method of claim 7 , wherein the formation of the membrane comprises dissolving the polymer of Formula 1 in an organic solvent to form a solution, and then making a film using the solution.
16. The method of claim 8 , wherein the compound of Formula 2 is poly(1,4-dimethylphenylene oxide) represented by Formula 2a, the compound of Formula 3 is represented by Formula 3a, and the polymer of Formula 1 is represented by Formula 1a:
wherein n is 3,000;
wherein a is an integer ranging from 500 to 100,000, b is an integer ranging from 1 to 50,000, and the mole ratio of a and b is 5:1;
where x is 1,500, y is 750, and z is 750.
17. A membrane-electrode assembly for a fuel cell, comprising:
an anode and a cathode facing each other; and
a polymer electrolyte membrane interposed between the anode and the cathode, the polymer electrolyte membrane comprising a polymer represented by Formula 1:
wherein R 1 to R 3 are the same or different, and are fluorine, hydrogen, or a substituted or unsubstituted alkyl group, and at least one of R 1 to R 3 is fluorine or an alkyl group substituted with fluorine;
R 4 to R 6 are independently —O—, —S—, —CO—, —SO 2 —, or —P(Ph)O where Ph is phenyl-;
R 7 to R 10 are independently hydrogen, a substituted or unsubstituted alkyl group, a substituted or unsubstituted heteroalkyl group, a substituted or unsubstituted aryl group, or a substituted or unsubstituted heteroaryl group;
R 11 is —O—, —S—, —CO—, or —SO 2 —;
l and m are independently an integer ranging from 0 to 24;
w is an integer ranging from 1 to 20;
k is an integer ranging from 1 to 1000;
x is an integer ranging from 100 to 100,000;
y is an integer ranging from 1 to 10,000;
z is an integer ranging from 1 to 10,000; and
Y is a proton conductive group.
18. A fuel cell system comprising:
an electricity generating element generating electricity by fuel oxidation and oxidant reduction reactions, the electricity generating element comprising:
a membrane-electrode assembly comprising an anode and a cathode facing each other and a polymer electrolyte membrane interposed between the anode and the cathode, the polymer electrolyte membrane comprising a polymer represented by Formula 1:
R 1 to R 3 are the same or different, and are fluorine, hydrogen, or a substituted or unsubstituted alkyl group, and at least one of R 1 to R 3 is fluorine or an alkyl group substituted with fluorine;
R 4 to R 6 are independently —O—, —S—, —CO—, —SO 2 —, or —P(Ph)O where Ph is phenyl-;
R 7 to R 10 are independently hydrogen, a substituted or unsubstituted alkyl group, a substituted or unsubstituted heteroalkyl group, a substituted or unsubstituted aryl group, or a substituted or unsubstituted heteroaryl group;
R 11 is —O—, —S—, —CO—, or —SO 2 —;
l and m are independently an integer ranging from 0 to 24;
w is an integer ranging from 1 to 20;
k is an integer ranging from 1 to 1000;
x is an integer ranging from 100 to 100,000;
y is an integer ranging from 1 to 10,000;
z is an integer ranging from 1 to 10,000; and
Y is a proton conductive group; and
separators positioned at each side of the membrane-electrode assembly;
a fuel supplier supplying the electricity generating element with a fuel; and
an oxidant supplier supplying the electricity generating element with an oxidant.