Method for manufacturing GRIN lens
A method for manufacturing a GRIN lens includes the steps of forming a wet gel provided with a concentration distribution having a different concentration of a refractive index distribution imparting metal that differs in concentration in a radial direction, drying the wet gel to form a dry gel having a bulk specific gravity ρ (g/cm 3 ), sintering the dry gel to form a GRIN lens base material and stretching the GRIN lens base material while heating. The method is characterized in that, in the step of sintering the dry gel, partial pressures of oxygen during sintering at 800° C. or higher are 10 −1 Pa or lower and also the relation between a rate of temperature increase v (° C./hr) and a bulk density ρ of the dry gel during sintering at 1,000 to 1,150° C. is defined by v≦10 5 *EXP (− 12 ρ). As a result of this, the GRIN lens, which has a large numerical aperture and a small diameter, can stably and easily be manufactured.
1. A method for manufacturing a GRIN lens comprising:
forming a wet gel including a refractive index distribution imparting metal, the wet gel having a concentration distribution of the refractive index distribution imparting metal which varies in a radial direction;
drying the wet gel to form a dry gel with a bulk density ρ of at least 0.6 g/cm 3 ;
sintering the dry gel to form a GRIN lens base material; and
stretching the GRIN lens base material while heating the GRIN lens base material,
wherein during the sintering operation, partial pressures of oxygen during sintering at 800° C. or higher are 10 −1 Pa or lower, and
wherein during the sintering operation, the relationship between a rate of temperature increase v in degrees Celsius per hour and the bulk density ρ in g/cm 3 of the dry gel during sintering at 1,000 to 1,150° C. is given by v≦10 5 *EXP(−12ρ).
2. The method for manufacturing the GRIN lens according to claim 1 , wherein during said sintering operation, partial pressures of oxygen are made 10 −1 Pa or lower by performing the sintering operation at 800° C. or higher in a helium atmosphere.
3. The method for manufacturing the GRIN lens according to claim 2 , wherein the refractive index distribution imparting metal is selected from the group consisting of titanium and tantalum.
4. The method for manufacturing the GRIN lens according to claim 1 , wherein the refractive index distribution imparting metal is selected from the group consisting of titanium and tantalum.
5. The method for manufacturing the GRIN lens according to claim 1 , wherein the numerical aperture of the GRIN lens is more than 0.4.
6. The method for manufacturing the GRIN lens according to claim 1 , wherein the numerical aperture of the GRIN lens is 0.47 to 0.48.
7. A method for manufacturing a GRIN lens comprising:
forming a wet gel including a refractive index distribution imparting metal, the wet gel having a concentration distribution of the refractive index distribution imparting metal which varies in a radial direction;
drying the wet gel to form a dry gel with a bulk density ρ of at least 0.6 g/cm 3 ;
sintering the dry gel to form a GRIN lens base material; and
stretching the GRIN lens base material while heating the GRIN lens base material,
wherein during the sintering operation, temperature is increased to 1,200° C., and between temperatures of 1,000 to 1,150° C. a rate of temperature increase v in degrees Celsius per hour satisfies the expression v≦10 5 *EXP(−12ρ), and
wherein during the sintering operation, partial pressures of oxygen at temperatures of 800° C. or higher are 10 −1 Pa or lower.
8. The method for manufacturing the GRIN lens according to claim 7 , wherein during said sintering operation, partial pressures of oxygen are made 10 −1 Pa or lower by performing the sintering operation at 800° C. or higher in a helium atmosphere.
9. The method for manufacturing the GRIN lens according to claim 8 , wherein the refractive index distribution imparting metal is selected from the group consisting of titanium and tantalum.
10. The method for manufacturing the GRIN lens according to claim 7 , wherein the refractive index distribution imparting metal is selected from the group consisting of titanium and tantalum.
11. The method for manufacturing the GRIN lens according to claim 7 , wherein the numerical aperture of the GRIN lens is more than 0.4.
12. The method for manufacturing the GRIN lens according to claim 7 , wherein the numerical aperture of the GRIN lens is 0.47 to 0.48.