US 7,947,523 · App. 12/424,827 · Granted May 24, 2011

Method for manufacturing photoelectric conversion device

Assignee: Semiconductor Energy Laboratory Co., Ltd.
View Patent ↗
Loading inventors, assignments & file history…
Monitor This Case
Get email alerts when status or documents change.
Order Certified Copies
Most orders are placed with the USPTO same day — all within 24 business hours.
Order via The Patent Place →
Pre-filled with this patent's details
Quick Facts
Patent No.
US 7,947,523
App. No.
12/424,827
Granted
May 24, 2011
Kind
B2
Abstract

An embrittlement layer is formed in the single crystal semiconductor substrate and a first impurity semiconductor layer, a first electrode, and an insulating layer are formed on one surface of the single crystal semiconductor substrate. After attaching the insulating layer and a supporting substrate to each other to bond the single crystal semiconductor substrate and the supporting substrate, the single crystal semiconductor substrate is separated along the embrittlement layer to form a stack including a first single crystal semiconductor layer. A first semiconductor layer and a second semiconductor layer are formed over the first single crystal semiconductor layer. A second single crystal semiconductor layer is formed by solid phase growth. A second impurity semiconductor layer having a conductivity type opposite to that of the first impurity semiconductor layer is formed on the second single crystal semiconductor layer. A second electrode is formed on the second impurity semiconductor layer.

Claims (140)

1. A method for manufacturing a photoelectric conversion device, comprising:

forming a first impurity semiconductor layer over a single crystal semicondcutor substrate;

irradiating the single crystal semiconductor substrate with ions to form an embrittlement layer in the single crystal semiconductor substrate;

forming a first electrode over the first impurity semiconductor layer;

forming an insulating layer over the first electrode;

attaching the insulating layer and a supporting substrate to each other to bond the single crystal semiconductor substrate and the supporting substrate and then separating the single crystal semiconductor substrate along the embrittlement layer, whereby a stack including the insulating layer, the first electrode, the first impurity semiconductor layer, and a first single crystal semiconductor layer is provided on the supporting substrate;

forming a first semiconductor layer over the first single crystal semiconductor layer;

forming a second semiconductor layer over the first semiconductor layer under a condition different from that of the first semiconductor layer;

forming a second single crystal semiconductor layer by improving crystallinity of the first semiconductor layer and the second semiconductor layer by solid phase growth;

forming a second impurity semiconductor layer having a conductivity type opposite to that of the first impurity semiconductor layer over the second single crystal semiconductor layer; and

forming a second electrode over the second impurity semiconductor layer.

2. The method for manufacturing a photoelectric conversion device, according to claim 1 ,

wherein the first semiconductor layer and the second semiconductor layer are formed such that crystallinity of the first semiconductor layer is higher than that of the second semiconductor layer.

3. The method for manufacturing a photoelectric conversion device, according to claim 1 ,

wherein the first semiconductor layer and the second semiconductor layer are formed such that hydrogen concentration of the first semiconductor layer is lower than that of the second semiconductor layer.

4. The method for manufacturing a photoelectric conversion device, according to claim 1 ,

wherein the first semiconductor layer is formed to a thickness of from 10 nm to 50 nm.

5. The method for manufacturing a photoelectric conversion device, according to claim 1 ,

wherein ions generated with a source gas containing hydrogen are used as the ions.

6. The method for manufacturing a photoelectric conversion device, according to claim 1 ,

wherein the first single crystal semiconductor layer and the second single crystal semiconductor layer are formed such that the total thickness of the first single crystal semiconductor layer and the second single crystal semiconductor layer is 800 nm or more.

7. The method for manufacturing a photoelectric conversion device, according to claim 1 ,

wherein the first impurity semiconductor layer is a p-type impurity semiconductor layer, and

wherein the second impurity semiconductor layer is an n-type impurity semiconductor layer.

8. The method for manufacturing a photoelectric conversion device, according to claim 1 ,

wherein the first semiconductor layer is formed by a plasma chemical vapor deposition method in which a flow ratio of a hydrogen gas to a silane based gas is 50:1 or more.

9. The method for manufacturing a photoelectric conversion device, according to claim 8 ,

wherein the silane based gas is silane or disilane.

10. The method for manufacturing a photoelectric conversion device, according to claim 8 or 9 ,

wherein the plasma chemical vapor deposition method is performed under a pressure of from 1 Pa to 10 3 Pa.

11. The method for manufacturing a photoelectric conversion device, according to claim 1 ,

wherein the first impurity semicondcutor layer and the second impurity semiconductor layer are formed by an ion implantation method or an ion doping method.

12. The method for manufacturing a photoelectric conversion device, according to claim 1 ,

wherein the first single crystal semiconductor layer is irradiated with a laser beam to repair or remove a crystal defect included in the first single crystal semicondcutor layer.

13. The method for manufacturing a photoelectric conversion device, according to claim 1 , wherein the second single crystal semicondcutor layer is formed by heating the first semiconductor layer and the second semiconductor layer by rapid thermal annealing.

14. A method for manufacturing a photoelectric conversion device, comprising:

irradiating a single crystal semiconductor substrate with ions to form an embrittlement layer in the single crystal semiconductor substrate;

forming a first impurity semiconductor layer over the single crystal semicondcutor substrate;

forming a first electrode over the first impurity semiconductor layer;

forming an insulating layer over the first electrode;

attaching the insulating layer and a supporting substrate to each other to bond the single crystal semiconductor substrate and the supporting substrate and then separating the single crystal semiconductor substrate along the embrittlement layer, whereby a stack including the insulating layer, the first electrode, the first impurity semiconductor layer, and a first single crystal semiconductor layer is provided on the supporting substrate;

forming a first semiconductor layer over the first single crystal semiconductor layer;

forming a second semiconductor layer over the first semiconductor layer under a condition different from that of the first semiconductor layer;

forming a second single crystal semiconductor layer by improving crystallinity of the first semiconductor layer and the second semiconductor layer by solid phase growth;

forming a second impurity semiconductor layer having a conductivity type opposite to that of the first impurity semiconductor layer over the second single crystal semiconductor layer; and

forming a second electrode over the second impurity semiconductor layer.

15. The method for manufacturing a photoelectric conversion device, according to claim 14 ,

wherein the first semiconductor layer and the second semiconductor layer are formed such that crystallinity of the first semiconductor layer is higher than that of the second semiconductor layer.

16. The method for manufacturing a photoelectric conversion device, according to claim 14 ,

wherein the first semiconductor layer and the second semiconductor layer are formed such that hydrogen concentration of the first semiconductor layer is lower than that of the second semiconductor layer.

17. The method for manufacturing a photoelectric conversion device, according to claim 14 ,

wherein the first semiconductor layer is formed to a thickness of from 10 nm to 50 nm.

18. The method for manufacturing a photoelectric conversion device, according to claim 14 ,

wherein ions generated with a source gas containing hydrogen are used as the ions.

19. The method for manufacturing a photoelectric conversion device, according to claim 14 ,

wherein the first single crystal semiconductor layer and the second single crystal semiconductor layer are formed such that the total thickness of the first single crystal semiconductor layer and the second single crystal semiconductor layer is 800 nm or more.

20. The method for manufacturing a photoelectric conversion device, according to claim 14 ,

wherein the first impurity semiconductor layer is a p-type impurity semiconductor layer, and

wherein the second impurity semiconductor layer is an n-type impurity semiconductor layer.

21. The method for manufacturing a photoelectric conversion device, according to claim 14 ,

wherein the first semiconductor layer is formed by a plasma chemical vapor deposition method in which a flow ratio of a hydrogen gas to a silane based gas is 50:1 or more.

22. The method for manufacturing a photoelectric conversion device, according to claim 21 ,

wherein the silane based gas is silane or disilane.

23. The method for manufacturing a photoelectric conversion device, according to claim 21 ,

wherein the plasma chemical vapor deposition method is performed under a pressure of from 1 Pa to 10 3 Pa.

24. The method for manufacturing a photoelectric conversion device, according to claim 14 ,

wherein the first impurity semicondcutor layer and the second impurity semiconductor layer are formed by an ion implantation method or an ion doping method.

25. The method for manufacturing a photoelectric conversion device, according to claim 14 ,

wherein the first single crystal semiconductor layer is irradiated with a laser beam to repair or remove a crystal defect included in the first single crystal semicondcutor layer.

26. The method for manufacturing a photoelectric conversion device, according to claim 14 , wherein the second single crystal semicondcutor layer is formed by heating the first semiconductor layer and the second semiconductor layer by rapid thermal annealing.

27. A method for manufacturing a photoelectric conversion device, comprising:

forming a first electrode over a single crystal semicondcutor substrate;

irradiating the single crystal semiconductor substrate with ions to form an embrittlement layer in the single crystal semiconductor substrate;

forming a first impurity semiconductor layer over the single crystal semicondcutor substrate;

forming an insulating layer over the first electrode;

attaching the insulating layer and a supporting substrate to each other to bond the single crystal semiconductor substrate and the supporting substrate and then separating the single crystal semiconductor substrate along the embrittlement layer, whereby a stack including the insulating layer, the first electrode, the first impurity semiconductor layer, and a first single crystal semiconductor layer is provided on the supporting substrate;

forming a first semiconductor layer over the first single crystal semiconductor layer;

forming a second semiconductor layer over the first semiconductor layer under a condition different from those of the first semiconductor layer;

forming a second single crystal semiconductor layer by improving crystallinity of the first semiconductor layer and the second semiconductor layer by solid phase growth;

forming a second impurity semiconductor layer having a conductivity type opposite to that of the first impurity semiconductor layer over the second single crystal semiconductor layer; and

forming a second electrode over the second impurity semiconductor layer.

28. The method for manufacturing a photoelectric conversion device, according to claim 27 ,

wherein the first semiconductor layer and the second semiconductor layer are formed such that crystallinity of the first semiconductor layer is higher than that of the second semiconductor layer.

29. The method for manufacturing a photoelectric conversion device, according to claim 27 ,

wherein the first semiconductor layer and the second semiconductor layer are formed such that hydrogen concentration of the first semiconductor layer is lower than that of the second semiconductor layer.

30. The method for manufacturing a photoelectric conversion device, according to claim 27 ,

wherein the first semiconductor layer is formed to a thickness of from 10 nm to 50 nm.

31. The method for manufacturing a photoelectric conversion device, according to claim 27 ,

wherein ions generated with a source gas containing hydrogen are used as the ions.

32. The method for manufacturing a photoelectric conversion device, according to claim 27 ,

wherein the first single crystal semiconductor layer and the second single crystal semiconductor layer are formed such that the total thickness of the first single crystal semiconductor layer and the second single crystal semiconductor layer is 800 nm or more.

33. The method for manufacturing a photoelectric conversion device, according to claim 27 ,

wherein the first impurity semiconductor layer is a p-type impurity semiconductor layer, and

wherein the second impurity semiconductor layer is an n-type impurity semiconductor layer.

34. The method for manufacturing a photoelectric conversion device, according to claim 27 ,

wherein the first semiconductor layer is formed by a plasma chemical vapor deposition method in which a flow ratio of a hydrogen gas to a silane based gas is 50:1 or more.

35. The method for manufacturing a photoelectric conversion device, according to claim 34 ,

wherein the silane based gas is silane or disilane.

36. The method for manufacturing a photoelectric conversion device, according to claim 34 ,

wherein the plasma chemical vapor deposition method is performed under a pressure of from 1 Pa to 10 3 Pa.

37. The method for manufacturing a photoelectric conversion device, according to claim 27 ,

wherein the first impurity semicondcutor layer and the second impurity semiconductor layer are formed by an ion implantation method or an ion doping method.

38. The method for manufacturing a photoelectric conversion device, according to claim 27 ,

wherein the first single crystal semiconductor layer is irradiated with a laser beam to repair or remove a crystal defect included in the first single crystal semicondcutor layer.

39. The method for manufacturing a photoelectric conversion device, according to claim 27 , wherein the second single crystal semicondcutor layer is formed by heating the first semiconductor layer and the second semiconductor layer by rapid thermal annealing.

40. A method for manufacturing a photoelectric conversion device, comprising:

forming a first electrode and a first impurity semiconductor layer over a single crystal semicondcutor substrate;

irradiating the single crystal semiconductor substrate with ions to form an embrittlement layer in the single crystal semiconductor substrate;

forming an insulating layer over the first electrode;

attaching the insulating layer and a supporting substrate to each other to bond the single crystal semiconductor substrate and the supporting substrate and then separating the single crystal semiconductor substrate along the embrittlement layer, whereby a stack including the insulating layer, the first electrode, the first impurity semiconductor layer, and a first single crystal semiconductor layer is provided on the supporting substrate;

forming a first semiconductor layer over the first single crystal semiconductor layer;

forming a second semiconductor layer over the first semiconductor layer under a condition different from that of the first semiconductor layer;

improving crystallinity of the first semiconductor layer and the second semiconductor layer by solid phase growth;

forming a second impurity semiconductor layer having a conductivity type opposite to that of the first impurity semiconductor layer over the second semiconductor layer; and

forming a second electrode over the second impurity semiconductor layer.

41. The method for manufacturing a photoelectric conversion device, according to claim 40 ,

wherein the first semiconductor layer and the second semiconductor layer are formed such that crystallinity of the first semiconductor layer is higher than that of the second semiconductor layer.

42. The method for manufacturing a photoelectric conversion device, according to claim 40 ,

wherein the first semiconductor layer and the second semiconductor layer are formed such that hydrogen concentration of the first semiconductor layer is lower than that of the second semiconductor layer.

43. The method for manufacturing a photoelectric conversion device, according to claim 40 ,

wherein the first semiconductor layer is formed to a thickness of from 10 nm to 50 nm.

44. The method for manufacturing a photoelectric conversion device, according to claim 40 ,

wherein ions generated with a source gas containing hydrogen are used as the ions.

45. The method for manufacturing a photoelectric conversion device, according to claim 40 ,

wherein the first single crystal semiconductor layer, the first semiconductor layer, and the second semiconductor layer are formed such that the total thickness thereof is 800 nm or more.

46. The method for manufacturing a photoelectric conversion device, according to claim 40 ,

wherein the first impurity semiconductor layer is a p-type impurity semiconductor layer, and

wherein the second impurity semiconductor layer is an n-type impurity semiconductor layer.

47. The method for manufacturing a photoelectric conversion device, according to claim 40 ,

wherein the first semiconductor layer is formed by a plasma chemical vapor deposition method in which a flow ratio of a hydrogen gas to a silane based gas is 50:1 or more.

48. The method for manufacturing a photoelectric conversion device, according to claim 47 ,

wherein the silane based gas is silane or disilane.

49. The method for manufacturing a photoelectric conversion device, according to claim 47 ,

wherein the plasma chemical vapor deposition method is performed under a pressure of from 1 Pa to 10 3 Pa.

50. The method for manufacturing a photoelectric conversion device, according to claim 40 ,

wherein the first impurity semicondcutor layer and the second impurity semiconductor layer are formed by an ion implantation method or an ion doping method.

51. The method for manufacturing a photoelectric conversion device, according to claim 40 ,

wherein the first single crystal semiconductor layer is irradiated with a laser beam to repair or remove a crystal defect included in the first single crystal semicondcutor layer.

52. The method for manufacturing a photoelectric conversion device, according to claim 40 ,

wherein the improving of crystallinity is performed by heating the first semiconductor layer and the second semiconductor layer by rapid thermal annealing.

Assignments (1)
ASSIGNMENT OF ASSIGNOR'S INTEREST Recorded Apr 16, 2009
From: KATO, SHO; TORIUMI, SATOSHI; ISAKA, FUMITO
To: SEMICONDUCTOR ENERGY LABORATORY CO., LTD.
Reel/Frame 022554/0928 →
Priority Claims (1)
JP 2008-114744 · Apr 25, 2008 · national
Continuity (1)
Related Publication 20090269875A1 · Oct 29, 2009