Water pressure transfer method and water pressure transfer article
In order to impart, concurrently with the transfer of a decorative layer, a surface protection function able to mechanically and chemically protect the decorative layer to be hydraulic-transferred of an article, a solventless type ultraviolet-curing resin composition is applied onto the dried printed pattern of a transfer film, an article is pushed into water along with the transfer film, with the printed pattern activated by a non-solvent activating component in the ultraviolet (uv)-curing resin composition and its adhesion force reproduced, and a ultraviolet ray is applied to the article to which the printed pattern, now impregnated and completely integrated with the uv-curing resin composition, has been transferred to thereby cure the uv-curing resin composition.
1. A water pressure transfer method for applying a transfer layer of a transfer film under water pressure to a surface of an article, the transfer layer being non-adhesive in a dry non-activated state and adhesive in a wet activated state, the method comprising the steps of:
a) providing a non-solvent type ultraviolet ray or electronic ray hardening resin composite including photo-polymerization pre-polymer, photo-polymerization monomer, photo-polymerization initiator and additives excluding solvent, said hardening resin composite having said photo-polymerization pre-polymer and photo-polymerization monomer present in the following blend ratio:
photo-polymerization pre-polymer 30-50 weight % and photo-polymerization monomer 20-70 weight % based upon the total weight of the hardening resin composite;
b) providing the transfer layer in the non-adhesive dry non-activated state;
c) coating said transfer layer with said hardening resin composite with said photo-polymerization monomer wetting said transfer layer to the adhesive wet activated state, said hardening resin composite permeating through said transfer layer to wholly unite with said transfer layer;
d) transferring said transfer layer from step (c) under water pressure to said surface of said article; and
e) irradiating said transferred layer from step (d) on said surface of said article with an ultraviolet ray or electronic ray to harden said hardening resin composite and form the transferred transfer layer wholly united with said hardening resin composite on said surface of said article.
2. A water pressure transfer method as set forth in claim 1 , wherein said transfer layer is a print pattern whereby a decorative layer is formed on the surface of said article.
3. A water pressure transfer method as set forth in claim 1 , wherein said transfer layer is a combination of a print pattern and a top-coating surface protection layer provided under said print pattern whereby a decorative layer having the top-coating surface protection layer thereon is formed on the surface of said article.
4. A water pressure transfer method as set forth in claim 1 , wherein said transfer layer is a surface protection layer whereby the surface protection layer is formed on the surface of said article.
5. A water pressure transfer article characterized by having a surface formed by the water pressure transfer method of any one of claims 1 , 2 , 3 , or 4 .
6. A water pressure transfer method for applying a transfer layer of a transfer film under water pressure to a surface of an article, the transfer layer being non-adhesive in a dry non-activated state and adhesive in a wet activated state, the method comprising the steps of:
a) providing a non-solvent type ultraviolet ray or electronic ray hardening resin composite including photo-polymerization pre-polymer, photo-polymerization monomer, photo-polymerization initiator and additives excluding solvent, said hardening resin composite having said photo-polymerization pre-polymer and photo-polymerization monomer present in the following blend ratio:
photo-polymerization pre-polymer 30-50 weight % and photo-polymerization monomer 20-70 weight % based upon the total weight of the hardening resin composite;
b) providing the transfer layer in the non-adhesive dry non-activated state as a dry print pattern, a dry top-coating surface protection layer or a combination of a dry print pattern and a dry top-coating surface protection layer;
c) coating said transfer layer with said hardening resin composite with said photo-polymerization monomer wetting said transfer layer to the adhesive wet activated state, said hardening resin composite permeating through said transfer layer to wholly unite with said transfer layer;
d) transferring said transfer layer from step (c) under water pressure to said surface of said article; and
e) irradiating said transferred layer from step (d) on said surface of said article with an ultraviolet ray or electronic ray to harden said hardening resin composite and form the transferred transfer layer wholly united with said hardening resin composite on said surface of said article.
7. A water pressure transfer method as set forth in claim 6 , wherein said hardening resin composite permeates through said transfer layer to wholly unite with said transfer layer to form a single layer.
8. A water pressure transfer method as set forth in claim 7 , wherein said hardening resin composite permeates and wholly unites with said transfer layer to form said single layer as a decorative layer on said surface of said article.
9. A water pressure transfer method as set forth in claim 1 , wherein said hardening resin composite permeates through said transfer layer to wholly unite with said transfer layer to form a single layer.
10. A water pressure transfer method as set forth in claim 9 , wherein said hardening resin composite permeates and wholly unites with said transfer layer to form said single layer as a decorative layer on said surface of said article.