Compound body and a process for the production of a mechanical connection
A compound body has a first body part ( 15 ) made of glass and a mechanical connection ( 20, 60 ) which is melted on the first body part ( 15 ) and contains aluminum.
1. Method for producing a flash lamp, comprising the steps of:
providing a first body part consisting of or containing glass and having an opening, and
attaching a connection to the first body part, wherein
aluminium having a purity of at least 99 weight percent is used for the connection,
the connection is heated beyond its melting point and melted onto the first body part,
the connection being purified from oxide components before melting it onto the first body part, and
the opening of the first body part being closed by the connection.
2. The method according to claim 1 , wherein after heating beyond its melting point the connection is purified from oxide components.
3. The method according to claim 1 , wherein the first body part is connected to a second body part by means of the connection.
4. The method according to claim 1 , wherein before producing the connection the first body part is at least regionally rounded where it contacts the connection, particularly by beginning to melt the body part.
5. The method according to claim 1 , wherein before attaching the connection to the first body part where it contacts the connection a material reinforcement is at least regionally formed, particularly by beginning to melt the body part.
6. The method according to claim 1 , wherein an auxiliary part consisting of material having a thermal expansion coefficient smaller than that of aluminium, preferably glass, is positioned in the opening and then connected to the first body part by means of the connection.
7. The method according to claim 1 , wherein before attaching the connection the aluminium-containing substance is mixed and melted with a grained and/or powdery filler having a thermal expansion coefficient smaller than that of aluminium.
8. The method according to claim 1 , wherein the melting of the connection onto the first body part is accomplished in the absence of oxygen, preferably in a protective gas atmosphere or in a vacuum.
9. The method according to claim 8 , wherein a gas is used as a protective gas with which the closed composite body is to be filled.
10. The method according to claim 1 , wherein the melting of the connection onto the first body part is accomplished at a temperature at which the connection has melted and at which the glass does not soften.
11. The method according to claim 10 , wherein the melting of the connection onto the first body part is accomplished at a temperature which facilitates the diffusion of alumina into the glass.
12. The method according to claim 1 , wherein during producing the mechanical connection the connection material and the first body part are gradually heated together.
13. The method according to claim 1 , wherein a tubular body part is used the end of which is flattened.
14. The method according to claim 13 , wherein the flattening is performed after attaching the connection, the glass being heated beyond its softening point before the flattening.
15. The method according to claim 13 , wherein the end the tube is bent.
16. The method according to claim 1 , wherein the connection is heated to at least 700° C. before it is melted onto the first body part.
17. The method according to claim 1 , wherein the heating of the connection and its purification from oxides is accomplished in a protective gas atmosphere.