Aromatic polycarbonate resin composition and production method thereof
According to the present invention, an aromatic polycarbonate resin composition comprising: a resin component (A) mainly comprising an aromatic polycarbonate; a reinforcing agent and/or a filler (B); and an aromatic sulfonic acid and/or an ester thereof (C), wherein a mixture consisting of said component (B) and said component (C) has a pH of 4 to 8 when measured in accordance with JIS-K5101, and said composition comprises 1 to 200 parts by weight of said component (B) and 0.001 to 5 parts by weight of said component (C) based on 100 parts by weight of said component (A) is provided.
1. A method of producing an aromatic polycarbonate resin composition comprising a resin component (A) comprising more than 50 parts by weight of an aromatic polycarbonate; a reinforcing agent and/or a filler (B); and an aromatic sulfonic acid and/or an ester thereof (C) by using a melt kneading apparatus, wherein said composition comprises 1 to 200 parts by weight of said component (B) and 0.001 to 5 parts by weight of said component (C) based on 100 parts by weight of said component (A),
said method comprising:
preparing a mixture consisting of said component (B) and said component (C) in advance, wherein said mixture of said component (B) and said component (C) has a pH of 4 to 8 when measured in accordance with JIS-K5101; and then
feeding said component (A) and said mixture consisting of said component (B) and said component (C) to said melt kneading apparatus to melt knead them.
2. The method according to claim 1 , wherein said component (B) is at least one member selected from a group consisting of glass fiber, glass flake, carbon fiber, talc and mica.
3. The method according to claim 1 , wherein 0.1 to 30 parts by weight of titanium oxide (D) is added to the mixture of component (B) and component (C) prior to feeding to the melt kneading apparatus.
4. The method according to claim 1 , wherein 0.01 to 1 part by weight of a fluoropolymer (E) is added to the mixture of component (B) and component (C) prior to feeding to the melt kneading apparatus.
5. The method according to claim 3 , wherein
0.01 to 1 part by weight of a fluoropolymer (E) is added to the mixture of component (B) and component (C) prior to feeding to the melt kneading apparatus.
6. The method according to claim 4 , wherein an aqueous dispersion of a fluoropolymer is used as said component (E).
7. The method according to claim 5 , wherein an aqueous dispersion of a fluoropolymer is used as said component (E).
8. The method according to claim 1 , wherein said composition comprises 0.005 to 3 parts by weight of said component (C) based on 100 parts by weight of said component (A).