Thin film field effect transistor with amorphous oxide active layer and display using the same
A TFT is provided which includes, on a substrate, at least a gate electrode, a gate insulating layer, an active layer containing an amorphous oxide semiconductor, a source electrode, and a drain electrode, wherein a carrier concentration of the active layer is 3×10 17 cm −3 or more and a film thickness of the active layer is 0.5 nm or more and less than 10 nm. A TFT is provided which has a low OFF current and a high ON-OFF ratio, and is improved in environmental temperature dependency. Also, a display using the TFT is provided.
1. A thin film field effect transistor comprising, on a substrate, at least a gate electrode, a gate insulating layer, an active layer containing an amorphous oxide semiconductor, a source electrode, and a drain electrode; wherein a carrier concentration of the active layer, determined by Hall effect measurement under an environment of 20° C., is 1×10 18 cm −3 or more, and a film thickness of the active layer is 0.5 nm or more and less than 10 nm.
2. The thin film field effect transistor according to claim 1 , wherein a roughness of an interface between the gate insulating layer and the active layer is less than 2 nm.
3. The thin film field effect transistor according to claim 1 , wherein the substrate is a flexible resin substrate.
4. A display using the thin film field effect transistor according to claim 1 .
5. The thin film field effect transistor according to claim 1 , wherein (i) the gate electrode, (ii) the gate insulating layer, (iii) the active layer, and (iv) the source electrode and the drain electrode, are provided on the substrate in a sequence from (i) to (iv), wherein (i) is closer to the substrate than (iv).
6. The thin film field effect transistor according to claim 1 , wherein the carrier concentration of the active layer is 1×10 19 cm −3 or more.
7. The thin film field effect transistor according to claim 1 , wherein the active layer contains at least one selected from the group consisting of In, Ga, Zn and Sn.
8. The thin film field effect transistor according to claim 7 , further comprising a low carrier concentration layer that is in contact with the active layer on the opposite side of the active layer from the gate insulating layer and has a carrier concentration of 10 16 cm −3 or less.
9. The thin film field effect transistor according to claim 7 , wherein the active layer contains In and Zn.
10. The thin film field effect transistor according to claim 9 , further comprising a low carrier concentration layer that is in contact with the active layer on the opposite side of the active layer from the gate insulating layer and has a carrier concentration of 10 16 cm −3 or less.
11. The thin film field effect transistor according to claim 1 , further comprising a low carrier concentration layer that is in contact with the active layer on the opposite side of the active layer from the gate insulating layer and has a carrier concentration of 10 16 cm −3 or less.
12. The thin film field effect transistor according to claim 11 , wherein the low carrier concentration layer is an amorphous oxide semiconductor layer.
13. The thin film field effect transistor according to claim 12 , wherein the amorphous oxide semiconductor in the low carrier concentration layer contains at least one selected from the group consisting of In, Ga, Zn and Sn.
14. The thin film field effect transistor according to claim 13 , wherein the amorphous oxide semiconductor in the low carrier concentration layer contains In and Zn.