Method and apparatus for tooth rejuvenation and hard tissue modification
The present invention is a number of methods and devices for tooth rejuvenation and hard tissue modification comprising applying a layer of a peroxide-free composition to a tooth surface. The applied composition comprises an aqueous solution of one or more edible acids. The composition has a pH selected from the range of about 0.5 to 5. After the treatment the composition is removed from the tooth surface. In various embodiments of the invention the pH of the composition can range between about 0.5 and 3, a narrower range being between 1 and 1.75. Hard tissue rejuvenation comprises forming a post-treatment layer having a composition which is different from that of the hard tissue by selectively heating a porous layer on the hard tissue.
1. A method of dental hard tissue modification comprising forming a superficial porous layer of the dental hard tissue and then selectively heating the superficial porous layer of the dental hard tissue to cause the superficial porous layer to fuse.
2. The method of claim 1 , wherein selectively heating comprises acting on the superficial porous layer with a pulsed laser.
3. The method of claim 1 , wherein a thickness of the superficial porous layer is between 0.5 μm and 100 μm.
4. The method of claim 1 , wherein selectively heating comprises heating the superficial porous layer to a temperature higher than a melting temperature of the dental hard tissue but less than 2000° C.
5. The method of claim 1 , further comprising forming the superficial porous layer of the dental hard tissue by using an acid before selectively heating the superficial porous layer.
6. The method of claim 1 , further comprising cooling the superficial porous layer with a cooling fluid.
7. A method of dental hard tissue modification comprising:
impregnating a superficial porous layer of the dental hard tissue with particles having a fluidity temperature about the same as a melting temperature of the dental hard tissue of the superficial porous layer; and
selectively heating the superficial porous layer to a temperature higher than the melting temperature of the dental hard tissue, causing the dental hard tissue and the particles to fuse.
8. The method of claim 7 , wherein the particles are inorganic particles.
9. The method of claim 8 , wherein the inorganic particles are crystal, ceramic, glass or their mixture.
10. The method of claim 8 , wherein the inorganic particles are name of Na 2 O—Al 2 O 3 —SiO 2 , Ca(PO 3 ), CaF 2 , Ca 10 (PO 4 ) 6 (OH) 2 , and Ca 10 (PO 4 ) 6 F 2 .
11. The method of claim 7 , wherein selectively heating the superficial porous layer comprises heating by acoustic energy, electromagnetic energy, comprising light, microwave, radio frequency, and electric current, and combinations thereof.
12. A method of dental hard tissue modification comprising:
impregnating a superficial porous layer of the dental hard tissue with particles having a fluidity temperature higher than a melting temperature of a hard tissue of the superficial porous layer; and
selectively heating the superficial porous layer to a temperature higher than the melting temperature of the dental hard tissues, but lower than the fluidity temperature of the particles.
13. The method of claim 12 , wherein selectively heating the superficial porous layer comprises heating by acoustic energy, electromagnetic energy, comprising light, microwave, radio frequency, and electric current, and combinations thereof.
14. The method of claim 12 , wherein the particles are inorganic particles.
15. The method of claim 14 , wherein the inorganic particles are made of crystal, ceramic, glass or their mixture.
16. The method of claim 15 , wherein the particles are made of quartz glass or sitall glass.
17. The method of claim 15 , wherein the particles are crystals selected from the group consisting of crystals of quartz, diamond, sapphire, topaz, amethyst, zircon, agate, granite, spinel, fianite, tanzanite, tourmaline and combinations thereof.
18. The method as in claim 1 , 7 or 12 , wherein the superficial porous layer is a carious lesion, open dentine, cementum, bone, or cartilage.
19. The method as in claim 1 , 7 or 12 , wherein the superficial porous layer is formed by applying the compound comprised of an acid.
20. The method as in claim 1 , 7 or 12 , wherein selectively heating the superficial porous layer is followed by active control cooling.
21. The method according to claim 20 , wherein active control cooling is provided by water.
22. A method of dental hard tissue modification comprising:
filling a superficial porous layer of the dental hard tissue with a fluidified material preheated above at least its fluidity temperature, wherein the fluidified material is glass, crystal or ceramic and mixture thereof; and
letting the fluidified material cool and solidify in the superficial porous layer.
23. A method of dental hard tissue modification comprising:
impregnating a porous surface of the dental hard tissue with particles having a fluidity temperature higher than a melting temperature of the dental hard tissue of the porous surface; and
filling the porous surface with a material preheated above its fluidity temperature, wherein the material is glass, crystal or ceramic or mixture thereof, and wherein the fluidity temperature of the material is lower than a melting temperature of the particles and that of the dental hard tissue.
24. A method of dental hard tissue modification comprising forming a post-treatment layer having a composition differing from that of the dental hard tissue by selectively heating a superficial porous layer on the dental hard tissue.
25. The method of claim 24 , comprising a step of forming the porous layer by applying to the dental hard tissue a composition having an acid before selectively heating the superficial porous layer.
26. The method of claim 24 , comprising a step of impregnating the superficial porous layer with particles before selectively heating the superficial porous layer.