Method for treating thermoplastic polyurethane golf ball covers
A method of forming a golf ball is disclosed herein. The method includes placing a golf ball precursor product with a cover comprising a thermoplastic polyurethane material and a dendritic polymer in a solution containing an isocyanate functionality reactive material. The precursor product is then removed and heated to remove solvent to prepare the precursor product for finishing.
1. A method of forming a golf ball, the method comprising:
placing a golf ball precursor product in a first solution to create a first solution covered golf ball precursor product, the golf ball precursor product comprising a cover comprising a thermoplastic aliphatic polyurethane material in an amount of 50 to 99.99 weight percent of the cover and a dendritic polymer, containing reactive end groups, in an amount of 0.01 to 50 weight percent of the cover, the first solution comprising chemical functionalities capable of reacting with the dendritic polymer;
removing the first solution covered golf ball precursor product from the first solution;
air drying the first solution covered golf ball precursor product to create a dried solution covered golf ball precursor product;
placing the dried solution covered golf ball precursor product in a second solution comprising an isocyanate, a dendritic polymer and a solvent to create a second solution covered golf ball precursor product;
and
heating the second solution covered golf ball precursor product to create a final golf ball precursor product.
2. The method according to claim 1 wherein the first solution further comprises a solvent selected from the group consisting of acetone, of methyl ethyl ketone and toluene.
3. The method according to claim 1 wherein the golf ball precursor product is placed in the first solution for one to two minutes.
4. The method according to claim 1 wherein the first solution covered golf ball precursor product is heated from two to four hours at a temperature ranging from 125° F. to 250° F.
5. The method according to claim 1 wherein the golf ball precursor product further comprises a core and a boundary layer formed over the core with the thermoplastic polyurethane cover formed over the boundary layer.
6. A method of forming a golf ball, the method comprising:
placing a golf ball precursor product in a first solution to create a first solution covered golf ball precursor product, the golf ball precursor product comprising a core, a boundary layer and a cover comprising a thermoplastic aliphatic polyurethane material in an amount of 50 to 99.99 weight percent of the cover and a dendritic polymer in an amount of 0.01 to 50 weight percent of the cover, the first solution comprising acetone and MDI;
removing the first solution covered golf ball precursor product from the first solution;
air drying the first solution covered golf ball precursor product to create a dried solution covered golf ball precursor product;
placing the dried solution covered golf ball precursor product in a second solution comprising an isocyanate, a dendritic polymer and a solvent to create a second solution covered golf ball precursor product;
and
heating the second solution covered golf ball precursor product to create a final golf ball precursor product, wherein the second solution covered golf ball precursor product is heated from two to four hours at a temperature ranging from 125° F. to 250° F.