Cement clinker and process for producing the same
A cement clinker which necessitates no considerable change in the main chemical components and mineral components of cement, is free from preheater coating problems and adverse influences on cement properties, and is effective in reducing the heat quantity required for burning; and a process for producing the cement clinker. In the process for cement clinker production a substance having a melting point higher than the temperature of a liquid phase of the cement clinker and serving as crystal nuclei for C 3 S is incorporated include a fine powder of refractory brick, particles of an ordinary Portland cement clinker, a fine powder of a high-early-strength Portland cement clinker, a high-early-strength Portland cement, and a fine powder of quicklime. Due to this, alite generation is accelerated even at a low temperature. As a result, high-quality clinker can be produced through burning using a small unit heat quantity and no decrease in cement quality results. The process contributes to a reduction in preheater coating amount and prolongation of the life of the refractory bricks.
1. A process for producing a cement clinker which contains alite, comprising burning a mixed raw material which is mixed at a raw material step, at a burning step, wherein cement clinker, cement, refractory brick or a combination thereof serving as a nucleus of generation of alite having a melting point higher than the temperature of a liquid phase of said cement clinker is incorporated into at least one of said cement raw material and said mixed raw material before said burning step.
2. The process for producing a cement clinker as set forth in claim 1 , wherein said cement clinker, cement, refractory brick or a combination thereof has a particle size of not more than 5 mm.
3. The process for producing a cement clinker as set forth in claim 1 , wherein said burning is performed by clinker burning equipment having a preheater, a burning furnace and a rotary kiln, and said cement clinker, cement, refractory brick or a combination thereof is charged into at least one of said preheater, said burning furnace, in a kiln-head or a kiln-tail of said rotary kiln in said clinker burning equipment.
4. The process for producing cement clinker as set forth in claim 1 , wherein said cement clinker, cement, refractory brick or a combination thereof has a particle size of not more than 0.01 mm.
5. The process for producing cement clinker as set forth in claim 1 , wherein the cement clinker, cement, refractory brick or a combination thereof is charged into a kiln-head of a rotary kiln so as to be landed at an area between where a liquid phase of a cement clinker in a burning step begins to generate and where alite begins to generate, thereby reducing a quantity of heat required for burning cement clinker, compared to before charging.
6. The process for producing cement clinker as set forth in claim 4 , wherein the cement clinker, cement, refractory brick or a combination thereof is charged into a kiln-head of a rotary kiln so as to be landed at an area between where a liquid phase of a cement clinker in a burning step begins to generate and where alite begins to generate, thereby reducing a quantity of heat required for burning cement clinker, compared to before charging.
7. A process for producing cement clinker which contains alite, the process comprising
charging a nucleus of generation of alite into a Portland cement raw material mixture, wherein said nucleus of generation of alite comprises cement clinker, cement, refractory brick, or a combination thereof, and
subsequently burning the resultant mixture of the nucleus of generation of alite and the Portland cement raw material mixture to produce cement clinker.
8. The process for producing a cement clinker as set forth in claim 7 , wherein said cement clinker, cement, refractory brick or a combination thereof has a particle size of not more than 5 mm.
9. The process for producing a cement clinker as set forth in claim 7 , wherein said burning is performed by clinker burning equipment having a preheater, a burning furnace and a rotary kiln, and said cement clinker, cement, refractory brick or a combination thereof is charged into at least one of said preheater, said burning furnace, in a kiln-head or a kiln-tail of said rotary kiln in said clinker burning equipment.
10. The process for producing cement clinker as set forth in claim 7 , wherein said cement clinker, cement, refractory brick or a combination thereof has a particle size of not more than 0.01 mm.
11. The process for producing cement clinker as set forth in claim 7 , wherein the cement clinker, cement, refractory brick or a combination thereof is charged into a kiln-head of a rotary kiln at a time between where a liquid phase of a cement clinker during said burning begins to form and where alite begins to form.
12. The process for producing cement clinker as set forth in claim 4 , wherein the cement clinker, cement, refractory brick or a combination thereof is charged into a kiln-head of a rotary kiln so as to be landed at an area between where a liquid phase of a cement clinker in a burning step begins to generate and where alite begins to generate, thereby reducing a quantity of heat required for burning cement clinker, compared to before charging.