Al—Mn based aluminum alloy composition combined with a homogenization treatment
An extrudable aluminum alloy billet includes an aluminum alloy composition including, in weight percent, between 0.90 and 1.30 manganese, between 0.05 and 0.25 iron, between 0.05 and 0.25 silicon, between 0.01 and 0.02 titanium, less than 0.01 copper, less than 0.01 nickel, and less than 0.05 magnesium, the aluminum alloy billet being homogenized at a temperature ranging between 550 and 600° C.
1. Aluminum alloy heat exchanger extruded tubes comprising an aluminum alloy composition consisting essentially of, in weight percent, between 0.90 and 1.30 manganese, between 0.05 and 0.25 iron, between 0.05 and 0.25 silicon, between 0.01 and 0.02 titanium, less than 0.01 copper, less than 0.01 nickel, and less than 0.05 magnesium, the aluminum alloy being cast as an ingot and homogenized at a homogenization temperature ranging between 550 and 600° C. before extruding the homogenized ingot into tubes.
2. Aluminum alloy heat exchanger extruded tubes as claimed in claim 1 , wherein the homogenized ingot has an ingot conductivity of 35 to 38 IACS.
3. Aluminum alloy heat exchanger extruded tubes as claimed in claim 1 , wherein the aluminum alloy ingot is homogenized at a homogenization temperature ranging between 560 and 590° C.
4. Aluminum alloy heat exchanger extruded tubes as claimed in claim 1 , wherein aluminum alloy ingot is homogenized for two to eight hours.
5. Aluminum alloy heat exchanger extruded tubes as claimed in claim 1 , wherein the homogenization is followed by a controlled cooling step carried at a cooling rate below 150° C. per hour.
6. Aluminum alloy heat exchanger extruded tubes as claimed in claim 1 , wherein the manganese content ranges between 0.90 and 1.20 wt %.
7. Aluminum alloy heat exchanger extruded tubes as claimed in claim 1 , wherein the extruded tubes have a wall thinner than 0.5 mm.
8. Aluminum alloy heat exchanger extruded tubes as claimed in claim 1 , wherein the extruded tubes are brazeable to at least one heat exchanger component.
9. Aluminum alloy heat exchanger extruded tubes as claimed in claim 1 , wherein the density of Mn dispersoids with a dcirc less than 0.5 microns in a square millimeter area is 18-41×104.
10. Aluminum alloy heat exchanger extruded tubes as claimed in claim 2 , wherein the aluminum alloy ingot is homogenized at a homogenization temperature ranging between 560 and 590° C.
11. Aluminum alloy heat exchanger extruded tubes as claimed in claim 2 , wherein aluminum alloy ingot is homogenized for two to eight hours.
12. Aluminum alloy heat exchanger extruded tubes as claimed in claim 2 , wherein the homogenization is followed by a controlled cooling step carried at a cooling rate below 150° C. per hour.
13. Aluminum alloy heat exchanger extruded tubes as claimed in claim 2 , wherein the manganese content ranges between 0.90 and 1.20 wt %.
14. Aluminum alloy heat exchanger extruded tubes as claimed in claim 2 , wherein the extruded tubes have a wall thinner than 0.5 mm.
15. Aluminum alloy heat exchanger extruded tubes as claimed in claim 2 wherein the extruded tubes are brazeable to at least one heat exchanger component.
16. Aluminum alloy heat exchanger extruded tubes as claimed in claim 2 , wherein the density of Mn dispersoids with a dcirc less than 0.5 microns in a square millimeter area is 18-41×104.