Amorphous alloy and manufacturing method thereof
View Patent ↗The present invention relates to an amorphous alloy and a method for manufacturing thereof. The amorphous alloy according to the present invention includes has a chemical formula of Feioo-a-b-c-d-e-f-gCraMobCcBaYeMflg. Here, the M is at least one selected from a group consisting of Al, Co, N1 and Ni, and the I is at least one selected from a group consisting of Mn, P, S, and O as impurities. The a, b, c, d, e, f, and g are satisfied with the compositions of 16.0 wt %≦a<22.0 wt %, 15.0 wt %<b≦27.0 wt %, 2.0 wt %≦c<3.5 wt %, 1.0 wt %<d≦1.5 wt %, 1.0 wt %<e≦3.5 wt %, 0.25 wt %<f≦3.0 wt %, and 0.01 wt %≦g<0.5 wt %, respectively.
1. An amorphous alloy having a chemical formula of Fe 100-a-b-c-d-e-f-g-h Cr a Mo b C c B d Y e M f I g N h ,
wherein the M is at least one selected from a group consisting of Al, Co, and Ni, wherein the I is at least one selected from a group consisting of Mn, P, S, and O as impurities, and wherein the a, b, c, d, e, f, g, and h are satisfied with the compositions of 16.0 wt %≦a≦22.0 wt %, 15.0 wt %≦b≦27.0 wt %, 2.0 wt %≦c≦3.5 wt %, 1.0 wt %≦d≦1.5 wt %, 1.0 wt %≦e≦3.5 wt %, 0 wt %≦f≦2.6 wt %, 0 wt %≦g≦0.5 wt %, and 0.4 wt %≦h≦1.0 wt % respectively.
2. The amorphous alloy of claim 1 , wherein the N is substantially 0.8 wt %.
3. The amorphous alloy of claim 1 , wherein an oxide film is formed on a surface of the amorphous alloy, and the oxide film comprises the N.
4. The amorphous alloy of claim 1 , wherein the Vickers microhardness of the amorphous alloy is 1000 kgf/mm 2 or more, and the compression strength of the amorphous alloy is in a range from 2500 MPa to 4000 MPa.
5. The amorphous alloy of claim 1 , wherein a wetting angle of the amorphous alloy is in a range from 80° to 100°.
6. The amorphous alloy of claim 1 , wherein the amorphous alloy is used as a material for a bipolar plate of a fuel cell.