Infiltrated carbon foam composites
An infiltrated carbon foam composite and method for making the composite is described. The infiltrated carbon foam composite may include a carbonized carbon aerogel in cells of a carbon foam body and a resin is infiltrated into the carbon foam body filling the cells of the carbon foam body and spaces around the carbonized carbon aerogel. The infiltrated carbon foam composites may be useful for mid-density ablative thermal protection systems.
1. An infiltrated carbon foam composite comprising:
a carbon foam body having a plurality of open cells distributed throughout the carbon foam body;
carbonized carbon aerogel located within at least a portion of the cells of the carbon foam body; and
a resin filling at least a portion of the carbon foam cells containing carbonized carbon aerogel.
2. The infiltrated carbon foam composite of claim 1 wherein the carbon foam body has a density ranging from about 0.05 g/cm 3 to about 0.8 g/cm 3 .
3. The infiltrated carbon foam composite of claim 1 wherein the carbon foam body has a density ranging from about 0.2 to about 0.6 g/cm 3 .
4. The infiltrated carbon foam composite of claim 1 wherein the resin is phenolic resin.
5. The carbon foam of claim 1 wherein the carbon foam body has a density ranging from about 0.2 to about 0.6 g/cm 3 , and wherein the resin is phenolic resin.
6. A method for making an infiltrated carbon foam composite comprising the steps of:
forming a carbon aerogel in the cells of a carbon foam body;
carbonizing the carbon aerogel within the cells of the carbon foam body; and
infiltrating the carbon foam body having carbonized carbon aerogel within cell of the carbon foam body with a resin.
7. The method of claim 6 wherein the carbon foam body has a density ranging from about 0.05 g/cm 3 to about 0.8 g/cm 3 .
8. The method of claim 6 wherein the carbon foam body has a density ranging from about 0.2 to about 0.6 g/cm 3 , and wherein the resin is phenolic resin.
9. The method of claim 6 wherein the step of forming a carbon aerogel in the cells of a carbon foam body forms a carbon aerogel in at least half of the cells of the carbon foam body.
10. The method of claim 6 wherein the step of forming a carbon aerogel in the cells of a carbon foam body forms a carbon aerogel in at least 75% of the cells of the carbon foam body.
11. The method of claim 6 wherein the step of forming a carbon aerogel in the cells of a carbon foam body forms a carbon aerogel in predominately all of the cells of the carbon foam body.