Method for twin roll casting of aluminum clad magnesium
A method for twin roll casting aluminum clad magnesium by joining one or more sheets of aluminum cladding to molten magnesium during twin roll casting. The method includes feeding aluminum cladding to at least one roll of a pair of rotating rolls, feeding a core of molten magnesium into a continuous casting mold formed by the roll, solidifying the magnesium core by heat extraction to the rolls and through the aluminum cladding, surface treating the aluminum cladding and the magnesium core to prevent inter-diffusion between the aluminum cladding and the magnesium core, bonding the aluminum cladding with the magnesium core and extruding the composite core and aluminum cladding out of the continuous casting mold by a casting load exerted by the rolls.
1. A method for manufacturing a clad magnesium sheet comprising the steps of:
feeding aluminum cladding to at least one roll of a pair of rotating rolls;
feeding a core of molten magnesium into a continuous casting mold formed by the roll;
solidifying the magnesium core by heat extraction to the rolls and through the aluminum cladding;
surface treating at least one of the aluminum cladding and the magnesium core to prevent inter-diffusion between the aluminum cladding and the magnesium core;
bonding the aluminum cladding with the magnesium core; and
extruding the composite magnesium core and aluminum cladding out of the continuous casting mold by a casting load exerted by the rolls,
thereby resulting in the clad magnesium sheet having improved paintability, weldability, bonding, corrosion and fire resistance, and surface modulus characteristics.
2. The method of claim 1 wherein the step of feeding aluminum cladding comprises feeding two separate strips of aluminum cladding, one for each opposite side of the core.
3. The method of claim 1 further comprising the step of interposing between the aluminum cladding and the magnesium core a barrier layer.
4. The method of claim 3 wherein the step of interposing the barrier layer is by thermal spray deposition.
5. A method of claim 1 further comprising the step of hot rolling the composite magnesium core and aluminum cladding in a water and oil emulsion.
6. The method of claim 1 wherein the step of feeding aluminum cladding to the roll is at an arc of contact of greater than 5 degrees while simultaneously applying tension to the aluminum cladding.
7. The method of claim 1 further comprising the step of surface treating both the aluminum cladding and the magnesium core prior to bonding.
8. The method of claim 7 wherein the surface preparation treatment is by a magnetically impelled arc cleaning head.
9. The method of claim 1 wherein the step of feeding aluminum cladding comprises unwinding a strip of aluminum cladding from a coil.
10. The method of claim 1 wherein the step of feeding aluminum cladding is by a thermal spray process.