Fast drying emulsion systems
The drying time for aqueous asphalt emulsions used in the roofing and other waterproofing industries is shortened by separately applying an emulsion breaking agent to the substrate to be waterproofed, to the aqueous asphalt emulsion after it is applied, or both.
1. A process for shortening the time needed for an aqueous asphalt emulsion to dry after the emulsion has been applied to a substrate by a single component sprayer, the process being carried out without simultaneous application to the substrate of an emulsion breaker along with the asphalt emulsion, the process comprising
contacting the emulsion with a reinforcing sheet comprising a fibrous or foraminous web or layer of material impregnated with a dried emulsion breaker.
2. The process of claim 1 , wherein the aqueous asphalt emulsion is applied to the substrate and thereafter the reinforcing sheet is applied to the aqueous asphalt emulsion.
3. The process of claim 1 , wherein the reinforcing sheet is applied to the substrate and thereafter the aqueous asphalt emulsion is applied to the reinforcing sheet.
4. The process of claim 1 , wherein the aqueous asphalt emulsion includes an anionic emulsifier and further wherein the emulsion breaker is selected from the group consisting of calcium chloride, calcium nitrate, aluminum chloride and ferric chloride.
5. The process of claim 1 , further comprising applying a reflective acrylic emulsion layer to the waterproofing asphalt layer.
6. The process of claim 5 , wherein the reflective acrylic emulsion layer is applied to the waterproofing asphalt layer within 24 hours of the application of the waterproofing asphalt layer to the substrate.
7. The process of claim 6 , wherein the acrylic emulsion layer is applied in an amount of ≧4 gal./sq.
8. The process of claim 5 , wherein the reflective acrylic emulsion layer is applied to a reinforcing sheet comprising a fibrous or foraminous web or layer of material impregnated with the emulsion breaker.
9. A process for shortening the time needed for an apueous asphalt emulsion to dry after the emulsion has been applied to a substrate comprising contacting the emulsion with a reinforcing sheet comprising a fibrous or foraminous web or layer of material impregnated with a dried emulsion breaker.