Single-stage thermal process for manufacturing transparent sintered spinel
View Patent ↗The invention provides a rapid and economical process for manufacturing a transparent, spinel based ceramic. A transparent body of sintered magnesium aluminate spinel having excellent optical and mechanical properties is provided in a single-stage thermal process.
1. A rapid process for manufacturing a transparent body of sintered magnesium aluminate spinel, comprising in one integrated stage
i) heating an approximately equimolar mixture of MgO and Al 2 O 3 powders with an additive of about 0.5 to 2 wt % LiF at a temperature-increase rate of from 70 to 200° C. up to a maximal temperature of about 1600° C.;
ii) applying, at said maximal temperature of about 1600° C., a gradually increasing axial pressure at a rate of from 5 to 10 MPa/min, up to a maximal pressure of between 50 and 100 MPa; and
iii) maintaining said maximal temperature and said maximal pressure for from 0.75 to 2 hours, followed by cooling to ambient temperature.
2. A process according to claim 1 , wherein said MgO and Al 2 O 3 powders have an average grain size not greater than 5 μm.
3. A process according to claim 1 , wherein said LiF is added to said mixture in an amount of 1 wt % of said mixture.
4. A process according to claim 1 , wherein said LiF is added as a powder or as a solution.
5. A process according to claim 1 , comprising heating said mixture at a temperature-increase rate of at least 80° C./min up to a maximal temperature of about 1600° C., applying gradually an axial pressure to reach 50 to 100 MPa at about 1600° C. at a rate that does not exceed 8±2 MPa/min, and maintaining the maximal temperature and pressure for 1 hour.
6. A process according to claim 1 , comprising Field Assisted Sintering Technology (FAST).
7. A process according to claim 1 , wherein said transparent spinel is obtained from said oxides within the total process time of less than 6 hours.