Basecoat and associated paperboard structure
A basecoat including a pigment blend of a coarse ground calcium carbonate and a hyperplaty clay having an average aspect ratio of at least about 40:1.
1. A paperboard structure comprising:
a paperboard substrate having a basis weight of at least 85 pounds per 3000 square feet; and
a basecoat applied to said paperboard substrate to form a layer on at least one surface of said paperboard substrate, said layer having a non-uniform cross-sectional thickness, wherein said cross-sectional thickness of said layer at each point on said paperboard substrate depends at least on a contour of said paperboard substrate at said point, said basecoat comprising a pigment blend including ground calcium carbonate and hyperplaty clay, wherein at most about 60 percent of said ground calcium carbonate has a particle size smaller than 2 microns, and wherein said hyperplaty clay has an average aspect ratio of at least about 40:1.
2. The paperboard structure of claim 1 wherein said average aspect ratio of said hyperplaty clay is at least about 70:1.
3. The paperboard structure of claim 1 wherein said average aspect ratio of said hyperplaty clay is at least about 90:1.
4. The paperboard structure of claim 1 wherein at most about 35 percent of said ground calcium carbonate has a particle size smaller than 2 microns.
5. The paperboard structure of claim 1 wherein said ground calcium carbonate comprises at least about 10 percent by weight of said pigment blend and at most about 60 percent by weight of said pigment blend.
6. The paperboard structure of claim 1 wherein said pigment blend consists essentially of said hyperplaty clay and said ground calcium carbonate.
7. The paperboard structure of claim 1 wherein said pigment blend has a sediment void volume of at least about 50 percent.
8. The paperboard structure of claim 1 wherein said paperboard substrate is formed as a web of fibers defining a plurality of pits in a surface thereof, and wherein said basecoat is received within said plurality of said pits without completely covering said surface.
9. The paperboard structure of claim 1 wherein said basecoat is applied to said paperboard substrate at a coat weight, per side, of at most about 9 pounds per 3000 square feet of said paperboard substrate.
10. The paperboard structure of claim 1 wherein said basecoat is applied to said paperboard substrate at a coat weight, per side, of at most about 8 pounds per 3000 square feet of said paperboard substrate.
11. The paperboard structure of claim 1 wherein said basecoat is applied to said paperboard substrate at a coat weight, per side, of at most about 7 pounds per 3000 square feet of said paperboard substrate.