Production of stable water dispersion epoxy phosphate ester resins and their aqueous coating compositions
View Patent ↗The present invention relates to novel compositions uniquely comprising combinations of different grades and/or type of epoxy resins and phosphoric acid into stable, water dispersion, epoxy phosphate ester copolymers. Aqueous thermosetting coating compositions, based on the novel epoxy phosphate ester resins, have the ability to reduce the requirements of curing temperature and time. The resultant coating films have superior protective properties, film properties, and wider applications than the conventional epoxy phosphate ester resins.
1. A single-stage process for the preparation of water-dispersible epoxy phosphate ester polymer substantially free of phosphoric acid from a mixture of epoxy resins selected from a group comprising diglycidyl ethers of bisphenols and having an average of greater than 1.5 epoxy groups and having one or more epoxy resins that is/are different in grade and/or type than at least one other epoxy resin in said mixture of epoxy resins, wherein each grade and/or type of epoxy resin has an average weight per epoxide equivalent (WPE) that is different from each other grade and/or type of epoxy resin in said mixture of epoxy resins, which comprises the step of:
reacting said mixture of epoxy resins with a phosphoric acid source material, selected from a group comprising orthophosphoric acid, phosphoric acid, polyphosphoric acid, superphosphoric acid, and other condensed forms of phosphoric acid.
2. The process in accordance with claim 1 wherein said epoxy resins used in the production of said epoxy phosphate ester polymers, are epoxy resins having the general structure:
and R represents a bisphenol residue,
and n is from 0 to 30.
3. The process in accordance with claim 2 , wherein the mixture of epoxy resins are at least two or more epoxy resins of the general structure (1) and (2), each epoxy resin consisting of between 1 to 99 weight percent of the epoxy polymers.
4. The process in accordance with claim 2 , wherein the epoxy polymer is prepared by mixing at least two different epoxy resins.
5. The process in accordance with claim 1 , wherein the phosphoric acid source material is used in an amount of from about 0.1-1 equivalent of phosphoric acid per equivalent of epoxy resin.
6. A water-borne coating composition comprising:
(a) the epoxy phosphate ester resin polymer of claim 1 ;
(b) at least one curing agent; and
(c) water.
7. The coating composition in accordance with claim 6 , further comprising an organic solvent.
8. The process in accordance with claim 1 , further including the step of neutralizing the epoxy phosphate ester polymer with one or more organic amines selected from a group comprising aliphatic mono- and polyfunctional amines, choline, guanidine, cycloaliphatic amines, aromatic amines, heterocylic amines and alkyl alcohol amines.
9. The process in accordance with claim 8 , wherein the organic amine is 2-amino-2-methyl-1-propanol.
10. The single-stage process in accordance with claim 1 , wherein the reacting step is carried out between 50° C. to 200° C. for a period of time between ½ to 6 hours.
11. A single-stage process for the preparation of water-dispersible epoxy phosphate ester polymers from at least two grades and/or types of epoxy resins selected from a group comprising diglycidyl ethers of bisphenols, with each grade and/or type of epoxy resin having an average of greater than 1.5 epoxy groups and which may possess a different epoxy per weight equivalent (WPE) for each grade and/or type of epoxy resin, which comprises the step of:
reacting said each grade and/or type of epoxy resin with a phosphoric acid source material selected from a group comprising orthophosphiric acid, phosphoric acid, polyphosphoric acid, superphosphoric acid, and other condensed forms of phosphoric acid at a strength of about 0.01-1 equivalent of phosphoric acid per equivalent of epoxy group to form the water-dispersible epoxy phosphate ester polymers substantially free of phosphoric acid, diesters and triesters of epoxy phosphate resins.
12. The process in accordance with claim 11 , wherein said each grade and/or type of epoxy resin which is used in the production of said water-dispersible epoxy phosphate ester polymer is selected from a group comprising a glycidyl ether of bisphenol A, a glycidyl ether of bisphenol K, a glycidyl ether of bisphenol F, a glycidyl ether of bisphenol S, and other glycidyl ethers of bisphenols having a molecular weight between 340 and 10,000.
13. The process in accordance with claim 11 , wherein said at least two grades and/or types of epoxy resin are epoxy resins having the general structure:
and R represents a bisphenol residue,
and n is from 0 to 30.
14. The process in accordance with claim 13 , wherein the epoxy polymers are prepared by mixing at least two different epoxy resin polymers.
15. The process in accordance with claim 11 , further including the step of neutralizing the epoxy phosphate ester polymer with one or more organic amines selected from a group comprising aliphatic mono- and polyfunctional amines, choline, guanidine, cycloaliphatic amines, aromatic amines, heterocylic amines and alkyl alcohol amines.
16. The process in accordance with claim 15 , wherein the organic amine is 2-amino-2-methyl-1-propanol.
17. The process in accordance with claim 15 , further including the step of adding water to the neutralized epoxy phosphate ester polymer.
18. The single-stage process in accordance with claim 11 , wherein the reacting step is carried out between 50° C. to 200° C. for a period of time between ½ to 6 hours.