Separation of carbon dioxide from gas mixtures by calcium based reaction separation
A reaction-based process has been developed for the selective removal of carbon dioxide (CO 2 ) from a multicomponent gas mixture to provide a gaseous stream depleted in CO2 compared to the inlet CO 2 concentration in the stream. The proposed process effects the separation of CO 2 from a mixture of gases (such as flue gas/fuel gas) by its reaction with metal oxides (such as calcium oxide). The Calcium based Reaction Separation for CO 2 (CaRS—CO 2 ) process consists of contacting a CO 2 laden gas with calcium oxide (CaO) in a reactor such that CaO captures the CO 2 by the formation of calcium carbonate (CaCOa). Once “spent”, CaCO 3 is regenerated by its calcination leading to the formation of fresh CaO sorbent and the evolution of a concentrated stream of CO 2 . The “regenerated” CaO is then recycled for the further capture of more CO 2 . This carbonation-calcination cycle forms the basis of the CaRS—CO 2 process. This process also identifies the application of a mesoporous CaCO 3 structure, developed by a process detailed elsewhere, that attains >90% conversion over multiple carbonation and calcination cycles. Lastly, thermal regeneration (calcination) under vacuum provided a better sorbent structure that maintained reproducible reactivity levels over multiple cycles.
1. A method for separating carbon dioxide and sulfur dioxide from a flow of gas comprising carbon dioxide and sulfur dioxide, said method comprising the steps of:
(a) directing said flow of gas to a gas-solid contact reactor, said gas-solid contact reactor containing a sorbent comprising a metal oxide;
(b) reacting said carbon dioxide and said sulfur dioxide with said sorbent so as to convert at least a portion of said sorbent to a metal carbonate and at least a portion of said sorbent to a metal sulfate;
(c) directing at least a portion of said metal carbonate to a calcinator;
(d) calcining said metal carbonate so as to form said metal oxide and carbon dioxide; and
(e) replenishing said sorbent in said gas-solid reactor with said metal oxide formed in said calcinator.
2. The method according to claim 1 , additionally comprising the step of:
separating said metal carbonate from said flow of gas in a cyclone.
3. The method according to claim 1 , wherein said step of reacting said carbon dioxide and said sulfur dioxide with said sorbent occurs at a temperature in the range of from about 600 to about 650 degrees Celsius.
4. The method according to claim 1 , additionally comprising the step of:
sequestering said carbon dioxide formed in said calcinator.
5. The method according to claim 1 , wherein said metal oxide is calcium oxide that has a surface area of less than 22 m2/g, a pore volume of at least 0.005 cm3/g, and a mesoporous pore size distribution.
6. The method according to claim 1 , wherein said step of calcining said metal carbonate is conducted under at least partial vacuum.
7. The method according to claim 1 , wherein said step of calcining said metal carbonate is performed by steam.
8. The method according to claim 1 , wherein said metal oxide is selected from the group consisting of: ZnO, MgO, MnO2, NiO, CuO, PbO, and CaO.
9. The method according to claim 1 , wherein said sorbent has a sorption capacity of at least about 70 grams of carbon dioxide per kilogram of sorbent.
10. The method according to claim 1 , wherein said sorbent has a sorption capacity of at least about 300 grams of carbon dioxide per kilogram of sorbent.
11. The method according to claim 1 , wherein said sorbent has substantially the same sorption capacity after calcining as said sorbent had prior to absorbing said carbon dioxide.
12. The method according to claim 1 , wherein said step of calcining said metal carbonate occurs at a temperature in the range of from about 800 to about 850 degrees Celsius.
13. A facility practicing the method according to claim 1 .