Polyether polyol, rigid polyurethane foam and processes for production thereof
Highly-functionalized, low-viscosity polyether polyols are obtained by dehydration condensation reaction of alcohols. The polyether polyols are obtained by dehydration condensation of glycerin and monohydric and/or dihydric alcohol with the glycerin percentage being more than 50 mol % relative to 100 mol % of the total of the glycerin and alcohol. The glycerin may be crude glycerin obtained by hydrolysis or alcoholysis of natural fat and oils.
1. A polyether polyol obtained by dehydration condensation of glycerin and monohydric and/or dihydric alcohol with the glycerin percentage being in the range of more than 50 mol % to not more than 95 mol % relative to 100 mol % of the total of the glycerin and alcohol,
wherein the polyether polyol has a hydroxyl value of 200 to 1200 mg KOH/g and a viscosity at 25° C. of not more than 50000 mPa·s.
2. The polyether polyol according to claim 1 , which has an average number of hydroxyl groups per molecule of not less than 3.
3. The polyether polyol according to claim 1 , wherein the glycerin is crude glycerin obtained by hydrolysis or alcoholysis of natural fat and oils.
4. A process for producing the polyether polyols described in claim 1 , which comprises dehydration condensing glycerin and monohydric and/or dihydric alcohol with the glycerin percentage being in the range of more than 50 mol % to not more than 95 mol % relative to 100 mol % of the total of the glycerin and alcohol.
5. A process for producing the polyether polyols described in claim 1 , which comprises dehydration condensing glycerin to produce a condensate, and dehydration condensing the condensate and monohydric and/or dihydric alcohol with the glycerin being used at a percentage in the range of more than 50 mol % to not more than 95 mol % relative to 100 mol % of the total of the glycerin and alcohol.
6. The process for producing the polyether polyols according to claim 4 or 5 , wherein the glycerin is crude glycerin obtained by hydrolysis or alcoholysis of natural fat and oils.
7. A rigid polyurethane foam obtained by reacting a polyol component comprising the polyether polyol of claim 1 and a polyisocyanate in the presence of a catalyst, a foaming agent and a foam stabilizer.
8. A rigid polyurethane foam obtained by reacting a polyol component comprising the polyether polyol of claim 3 and a polyisocyanate in the presence of a catalyst, a foaming agent and a foam stabilizer.
9. A process for producing rigid polyurethane foams, which comprises reacting a polyol component comprising the polyether polyol of claim 1 and a polyisocyanate in the presence of a catalyst, a foaming agent and a foam stabilizer.
10. A process for producing rigid polyurethane foams, which comprises reacting a polyol component comprising the polyether polyol of claim 3 and a polyisocyanate in the presence of a catalyst, a foaming agent and a foam stabilizer.