Copolymers of epsilon-caprolactone and glycolide for melt blown nonwoven applications
Copolymers exhibiting the following combinations of properties, including without limitation, ε-caprolactone in an amount ranging from about 12 to about 70 mole percent, glycolide in an amount ranging from about 30 to about 88 mole percent, crystallinity ranging from about 10 to about 50% as measured by WAXD or about 10 to about 50 J/g as measured by DSC, and an inherent viscosity ranging from about 0.5 to about 1.45 dL/g as measured in a 0.1 g/dl solution of HFIP at 25° C.; a method for melt blowing such copolymers and nonwoven constructs produced therefrom are described herein.
1. A copolymer for use in the production of nonwoven constructs, the copolymer comprising ε-caprolactone in an amount ranging from 12 to 20 mole percent, glycolide in an amount ranging from 80 to 88 mole percent, crystallinity ranging from 10 and 50% as measured by WAXD or 10 to 50 J/g as measured by DSC, and an inherent viscosity ranging from 0.5 to 1.45 dL/g as measured in a 0.1 g/dl solution of HFIP at 25° C., wherein the copolymer is the reaction product of a predominant amount of a prepolymer of ε-caprolactone and glycolide having a mole ratio of ε-caprolactone/glycolide of less than 30/70, with a balance of glycolide.
2. The copolymer of claim 1 , wherein the crystallinity ranging from 10 to 35% as measured by WAXD or 10 to 35 J/g as measured by DSC.
3. The copolymer of claim 2 , wherein the crystallinity ranging from 25 to 35% as measured by WAXD or 25 to 35 J/g as measured by DSC.
4. The copolymer of claim 1 , wherein the inherent viscosity ranging from 0.74 to 1.45 dL/g as measured in a 0.1 g/dL solution of HFIP at 25° C.