Synthesis of polymer coated ceria nanoparticles for biomedical applications
View Patent ↗Procedures and methods for synthesizing biodegradable polymer coated nanoceria result in stable nanoparticle preparations in aqueous systems and physiological relevant colloidal solutions, such as phosphate buffer saline. The coated nanoceria preparations increase the nanoparticle concentration in aqueous or colloidal solutions as most needed for antioxidant, free-radical scavenger, and autocatalytic biomedical applications, including, biological, pharmacological and potential clinical use. To meet this need, a facile synthetic procedure for preparation of a biodegradable polymer-coated nanoceria is disclosed; the preferred biodegradable polymer is dextran. The synthesis method occurs under ambient conditions in an aqueous phase without the use of surfactants and results in a monodispersed preparation that is dextran-coated as determined by dynamic light scattering (DLS). Preliminary characterization of polymer coated nanoceria by XPS, TEM, XRD, and the like shows that these nanoparticles have the necessary physical properties for the desired biological potency, such as Ce +4 /Ce +3 mixed valence state.
1. A method for the synthesis of a plurality of polymer-coated cerium oxide nanoparticles coated with a biodegradable polymer for antioxidant, free-radical scavenger and autocatalytic biomedical applications, comprising the steps of:
a) preparing an aqueous cerium nitrate solution containing approximately 2.0 to approximately 3.0 grams of cerium nitrate to approximately 5 ml of water;
b) mixing the aqueous cerium nitrate solution with a biodegradable polymer to form mixture (I);
c) adding mixture (I) dropwise to an ammonium hydroxide solution while continuously stirring to form mixture (II);
d) centrifuging the mixture (II) containing ammonium hydroxide to settle any debris or large particles;
e) purifying the centrifuged mixture of d) by ultrafiltration;
f) recovering a plurality of non-agglomerated, polymer-coated cerium oxide nanoparticles coated with the biodegradable polymer wherein the plurality of polymer-coated cerium oxide nanoparticles has a UV profile exhibiting strong absorption below approximately 400 nm with peak absorption at approximately 300 nm; and
g) contacting isolated biological cells with the plurality of polymer-coated cerium oxide nanoparticles wherein the antioxidant, free-radical scavenging and autocatalytic properties of the polymer-coated cerium oxide nanoparticles are unchanged from uncoated cerium oxide nanoparticles.
2. The method of claim 1 , wherein the biodegradable polymer is selected from the group consisting of a carbohydrate polymer, a synthetic polyol, a carboxylated polymer, and derivatives thereof.
3. The method of claim 2 , wherein the carboxylated polymer is polyacrylic acid.
4. The method of claim 2 , wherein the carboxylated polymer is reacted with a diamine selected from at least one of ethylene diamine, propylene diamine and hexane diamine, to provide an aminated cerium oxide nanoparticle in a reaction that eliminates the need for polymer crosslinking.
5. The method of claim 2 , wherein the carbohydrate polymer is a polysaccharide.
6. The method of claim 5 , wherein the polysaccharide is selected from the group consisting of dextran, arabinogalactan and chitosan.
7. The method of claim 6 , wherein the polysaccharide is dextran.
8. A composition of matter that is useful as a potent antioxidant in biomedical applications that comprises:
a plurality of polymer-coated nanoceria particles in contact with isolated biological cells wherein the plurality of polymer-coated nanoceria particles is coated with a biodegradable polymer selected from at least one of a carbohydrate polymer, a synthetic polyol, a carboxylated polymer, and derivatives thereof wherein the plurality of polymer-coated cerium oxide nanoparticles has a UV profile exhibiting strong absorption below approximately 400 nm with peak absorption at approximately 300 nm and the antioxidant properties of the polymer-coated cerium oxide nanoparticles are unchanged from uncoated cerium oxide nanoparticles.
9. The composition of claim 8 , wherein the carboxylated polymer is polyacrylic acid and derivatives thereof.
10. The composition of claim 8 , wherein the carbohydrate polymer is a polysaccharide and derivatives thereof.
11. The composition of claim 10 , wherein the polysaccharide is selected from the group consisting of dextran, arabinogalactan, chitosan and derivatives thereof.
12. The composition of claim 11 , wherein the polysaccharide is dextran and derivatives thereof.
13. The composition of claim 12 , wherein the plurality of dextran-coated cerium oxide nanoparticles has a UV profile exhibiting strong absorption below approximately 400 nm with peak absorption at approximately 300 nm.
14. The composition of claim 12 , wherein the physical properties of the dextran-coated cerium nanoparticles replicate the physical properties of the uncoated nanoceria particles for therapeutic applications as an antioxidant, free-radical scavenger and autocatalytic agent.
15. The composition of claim 12 , wherein the plurality of dextran-coated cerium oxide nanoparticles form a colloidal suspension that is stable in water.
16. The composition of claim 12 , wherein the plurality of dextran-coated cerium oxide nanoparticles form a colloidal suspension that is stable in a phosphate buffer saline solution.
17. A composition of matter that is useful as an antioxidant, free-radical scavenger and autocatalyst in biomedical applications that comprises:
a plurality of polymer-coated nanoceria particles in contact with isolated biological cells wherein the plurality of polymer-coated nanoceria particles is coated with a crosslinked-aminated biodegradable polymer selected from at least one of a carbohydrate polymer, a synthetic polyol, a carboxylated polymer, and derivatives thereof wherein the plurality of crosslinked-animated polymer-coated cerium oxide nanoparticles has a UV profile exhibiting strong absorption below approximately 400 nm with peak absorption at approximately 300 nm and the antioxidant, free-radical scavenging and autocatalytic properties of the polymer-coated cerium oxide nanoparticles are unchanged from uncoated cerium oxide nanoparticles.
18. The composition of claim 17 , wherein the carbohydrate polymer is a polysaccharide.
19. The composition of claim 18 , wherein the polysaccharide is selected from the group consisting of dextran, arabinogalactan and chitosan.
20. The composition of claim 19 , wherein the polysaccharide is dextran.
21. The composition of claim 20 , wherein the plurality of dextran-coated cerium oxide nanoparticles has a UV profile exhibiting strong absorption below approximately 400 nm with peak absorption at approximately 300 nm.
22. The composition of claim 20 , wherein the physical properties of the dextran-coated cerium nanoparticles replicate the physical properties of the uncoated nanoceria particles for therapeutic applications as an antioxidant, free-radical scavenger and autocatalytic agent.
23. The composition of claim 20 , wherein the plurality of dextran-coated cerium oxide nanoparticles form a colloidal suspension that is stable in water.
24. The composition of claim 20 , wherein the plurality of dextran-coated cerium oxide nanoparticles form a colloidal suspension that is stable in a phosphate buffer saline solution.
25. A composition of matter that is useful as an antioxidant, free-radical scavenger and autocatalyst in biomedical applications that comprises:
a plurality of polymer-coated nanoceria particles in contact with mammalian cells in need of antioxidant treatments to prolong cell life wherein the plurality of polymer-coated nanoceria particles is coated with a crosslinked-aminated biodegradable polymer selected from at least one of a carbohydrate polymer, a synthetic polyol, a carboxylated polymer, and derivatives thereof wherein the plurality of crosslinked-animated polymer-coated cerium oxide nanoparticles has a UV profile exhibiting strong absorption below approximately 400 nm with peak absorption at approximately 300 nm and the antioxidant, free-radical scavenging and autocatalytic properties of the polymer-coated cerium oxide nanoparticles are unchanged from uncoated cerium oxide nanoparticles.